Wire Wound Common Mode Choke - YLCM1006C Series
The YLCM1006C Series is a wire wound common mode choke featuring SMD construction and a low profile. It offers high impedance, excellent frequency characteristics, self-electromagnetic shielding, and low magnetic flux leakage. This product is designed for applications such as LED lighting, TV games, and monitors, primarily to suppress EMI common-mode noise.
Product Attributes
- Brand: YJY ()
- Origin: China
- Core Material: Ferrite
- Case Material: DAP-WH9100
- Wire Material: P180 Grd1
- Solder Material: Sn99.3:Cu0.7
- Adhesive Material: XNR-3614
- Ink Color: White
Technical Specifications
| Type | Inductance L1=L2 (uH) @100KHz/0.1V | DC Resistance (m) Max. | Rated Current (A) Max. | Hi-Pot (Vac) 3mA/1S | Impedance () Min. | Freq. Range (MHz) | Dimensions (mm) A | Dimensions (mm) B | Dimensions (mm) C Max | Dimensions (mm) D Max | Dimensions (mm) E Max | Dimensions (mm) F Ref |
| YLCM1006C-471T | 47040% | 65 | 1.60 | 1000 | 900 | 2~40 | 10.00.5 | 8.70.5 | 6.5 | 6.220.1 | 7.620.1 | 1.4 |
Operating Conditions & Reliability
Rated Current: Temp. rise 40 Typ
Operating Temperature: -20 up to +125
Storage Temperature: -20 up to +40, 75% RH max.
Reliability Testing:
- Operating Temperature: -20 to +125 (Contain Heating coil)
- Appearance Inspection: No external defects by visual inspection
- Terminal Strength: After soldering, withstands 10N (1.02kg) push in two directions (X, Y) for 10+/-2 sec. Terminal should not peel off.
- Heat endurance of reflow soldering: Refer to figure
- Insulating resistance: Over 100 M at 100V D.C. between wire and core.
- Dielectric Strength: Apply at 0.5KV 3mA for 1 minute between wire and core.
- Temperature characteristics: Inductance coefficient (0~2,000) 10 / (-20 ~ +125 )
- Humidity characteristics: Inductance deviation within 10% after 96 hours in 90~95% relative humidity at 40 2 and 1 hour drying under normal condition.
Taping & Reel Dimensions
| Type | Taping W (mm) | Taping A (mm) | Taping B (mm) | Taping D (mm) | Taping P (mm) | Taping K (mm) | Taping MPQ | Reel W (mm) | Reel W1 (mm) | Reel A (mm) | Reel B (mm) | Reel C (mm) | Reel D (mm) | |
| YLCM1006C | 24.00.3 | 10.60.3 | 11.50.1 | 11.50.1 | 160.1 | 5.00.1 | 0.400.05 | 800 | 3302.0 | 24.41.5 | 30.4 MAX | 23.9 MIN | 13.00.50 | 21.00.80 |
Taping Details
Direction of rolling: (Refer to figure)
Cover tape peel off condition: Cover tape peel force shall be 0.1N to 1.3N. Reference peel speed 30010mm/min.