Specifications
Power(Watts):
100mW
Resistance:
6.65kΩ
Voltage Rating:
75V
Operating Temperature:
-55℃~+155℃
Type:
Thick Film Resistor
Temperature Coefficient:
±100ppm/℃
Tolerance:
±1%
Mfr. Part #:
SCR0603F6K65
Package:
0603
Key Attributes
Model Number:
SCR0603F6K65
Product Description
Thick Film Chip Resistors
This document specifies the SCR series lead-free, halogen-free thick film chip resistors. These are general-purpose resistors designed for a wide range of applications. The resistors are manufactured to meet RoHS requirements, with lead in the resistive layer glass material being exempt.
Product Attributes
- Brand: VIC (implied by URL and development vision)
- Origin: Anhui XiangSheng Technology Co., Ltd.
- Material: Thick Film
- Certifications: RoHS compliant (lead-free, halogen-free)
Technical Specifications
| Type | Size | Tolerance | Resistance Range | Rated Power (W) | Max. Rated Voltage (V) | Max. Overload Voltage (V) | T.C.R (ppm/) | Operating Temp. Range | JUMPER (0) Resistance |
|---|---|---|---|---|---|---|---|---|---|
| SCR 0402 | 0402 | J (5%) | 1R9.1 (E-24) | 1 | 50 | 100 | 400 | -55~ +155 | 50m MAX. |
| SCR 0402 | 0402 | F (1%) / D (0.5%) | 10R10M (E-24, E-96) | 1 | 50 | 100 | 100 | 50m MAX. | |
| SCR 0603 | 0603 | J (5%) | 1R9.1 (E-24) | 1 | 75 | 150 | 400 | -55~ +155 | 50m MAX. |
| SCR 0603 | 0603 | F (1%) / D (0.5%) | 10R10M (E-24, E-96) | 1 | 75 | 150 | 100 | 50m MAX. | |
| SCR 0805 | 0805 | J (5%) | 1R9.1 (E-24) | 1 | 150 | 300 | 400 | -55~ +155 | 50m MAX. |
| SCR 0805 | 0805 | F (1%) / D (0.5%) | 10R10M (E-24, E-96) | 1 | 150 | 300 | 100 | 50m MAX. | |
| SCR 1206 | 1206 | J (5%) | 1R9.1 (E-24) | 1 | 200 | 400 | 400 | -55~ +155 | 50m MAX. |
| SCR 1206 | 1206 | F (1%) / D (0.5%) | 10R10M (E-24, E-96) | 1 | 200 | 400 | 100 | 50m MAX. | |
| SCR 1210 | 1210 | J (5%) | 1R9.1 (E-24) | 1 | 200 | 400 | 400 | -55~ +155 | 50m MAX. |
| SCR 1210 | 1210 | F (1%) / D (0.5%) | 10R10M (E-24, E-96) | 1 | 200 | 400 | 100 | 50m MAX. | |
| SCR 2010 | 2010 | J (5%) | 1R9.1 (E-24) | 3 | 200 | 400 | 400 | -55~ +155 | 50m MAX. |
| SCR 2010 | 2010 | F (1%) / D (0.5%) | 10R10M (E-24, E-96) | 3 | 200 | 400 | 100 | 50m MAX. | |
| SCR 2512 | 2512 | J (5%) | 1R9.1 (E-24) | 1 | 200 | 400 | 400 | -55~ +155 | 50m MAX. |
| SCR 2512 | 2512 | F (1%) / D (0.5%) | 10R10M (E-24, E-96) | 1 | 200 | 400 | 100 | 50m MAX. |
| Type | L (mm) | W (mm) | H (mm) | L1 (mm) | L2 (mm) |
|---|---|---|---|---|---|
| 0201 | 0.600.03 | 0.30.03 | 0.230.03 | 0.100.05 | 0.150.05 |
| 0402 | 1.000.10 | 0.500.05 | 0.300.05 | 0.200.10 | 0.250.10 |
| 0603 | 1.600.10 | 0.800.10 | 0.450.10 | 0.300.15 | 0.250.15 |
| 0805 | 2.000.10 | 1.250.10 | 0.500.10 | 0.350.20 | 0.350.20 |
| 1206 | 3.050.10 | 1.550.10 | 0.500.10 | 0.450.20 | 0.400.20 |
| 1210 | 3.050.10 | 2.600.15 | 0.550.10 | 0.450.20 | 0.500.20 |
| 2010 | 5.000.10 | 2.500.15 | 0.550.10 | 0.450.20 | 0.500.20 |
| 2512 | 6.350.10 | 3.100.15 | 0.550.10 | 0.600.20 | 0.500.20 |
| Test Item | Conditions | Specifications |
|---|---|---|
| Temperature Coefficient of Resistance (TCR) | Measured at -55 or +125 relative to room temperature. | Refer to 3. Specification Table |
| Short Time Overload | Applied 2.5 times rated voltage for 5 seconds, rest 30 minutes. | Resistance change rate: 0.5%/1%: (1.0%+0.05); 5%: (2.0%+0.10). Appearance: No damage, short circuit or burnout. |
| Intermittent Overload | 2.5x rated voltage, 1s ON, 25s OFF, 10000 cycles. | Resistance change rate: 1: (5.0%+0.10); <1: (5.0%+0.001). Appearance: No damage, short circuit or burnout. |
| Terminal Strength | Test 1: 5N force applied to back of resistor for 10 sec. Test 2: Gradually apply force to back of resistor. | Test 1: No damage, no side conductor detachment, no body fracture. Test 2: Pull force 5N. |
| Resistance to Solvent | Immersed in Isopropyl alcohol at 20~25 for 50.5 min, rest 48 hr. | Resistance change rate: (1.0%+0.05). Appearance: No damage, no G2 protective layer or tin layer leaching. |
| Solderability | Pre-treatment: PCT machine at 105, 100% RH, 1.22105 pa for 4 hours. Immerse in 2355 furnace for 2 seconds. | Soldered area > 95%. |
| Resistance to Soldering Heat | Test 1 (Solder pot): Immerse in 260+5/-0 for 10 sec, rest 60 min. Test 2 (Solder pot): Immerse in 260+5/-0 for 30 sec. Test 3 (Soldering iron): 35010 for 3 sec. | Test 1: Resistance change rate: 1: (1.0%+0.05); Electrode appearance: No abnormality, no side conductor detachment. Test 2: Soldered area > 95%; No underlying material visible at electrode edge. Test 3: Resistance change rate: 1: (1.0%+0.05); Electrode appearance: No abnormality, no side conductor detachment. |
| Bending Test | Weld resistor on bending test board, apply force to center. Downward depth: 0201/0402=5mm, 0603/0805=3mm, 1206+=2mm. | Resistance change rate: 1: (1.0%+0.05). Appearance: No damage, no side conductor detachment, no body fracture. |
| Resistance to Dry Heat | Oven at 1555 for 1000 hrs (RTT01 at 1253). | Resistance change rate: 0.1%/0.5%/1%: (1.0%+0.05); 2%/5%: (2.0%+0.10). Appearance: No damage, short circuit, or burnout. |
| Thermal Shock | -55 for 15 min, +125 for 15 min, 300 cycles. | Resistance change rate: 0.1%/0.5%/1%: (1.0%+0.05); 2%/5%: (2.0%+0.05). Appearance: No damage, short circuit, or burnout. |
| Moisture Load Life | 402, 90~95% RH, 90 min ON, 30 min OFF, 1000 hrs. | Resistance change rate: 1%: (1.0%+0.05); 5%: (2.0%+0.10). Appearance: No damage, short circuit, or burnout. |
| Load Life | 702 oven, 90 min ON, 30 min OFF, 1000 hrs. | Resistance change rate: 1%: (1.0%+0.05); 5%: (2.0%+0.10). Appearance: No damage, short circuit, or burnout. |