Specifications
Normal temperature Frequency Tolerance:
±20ppm
Frequency Stability:
±30ppm
Load Capacitance:
20pF
Operating Temperature:
-40℃~+85℃
Frequency:
12MHz
Mfr. Part #:
6I12000F20UCG
Package:
SMD5032-2P
Key Attributes
Model Number:
6I12000F20UCG
Product Description
QUARTZ CRYSTAL UNIT SERIES 6I, GLASS SEALED CERAMIC 5.0*3.2MM SURFACE MOUNT PACKAGE
The QUARTZ CRYSTAL UNIT SERIES 6I is a glass-sealed ceramic surface mount package measuring 5.0*3.2mm. It is designed for applications requiring precise frequency control, featuring a fundamental AT mode of vibration and a load capacitance of 20.0 PF. This series is suitable for operation within a wide temperature range of -40C to +85C and is available with RoHS, REACH, and HF compliance.
Product Attributes
- Brand: SJK
- Origin:
- Material: Glass Sealed Ceramic
- Package: 5.0*3.2mm Surface Mount
- Certifications: RoHS, REACH, HF
- Moisture Sensitivity Level: Level 1
- Minimum Packaging: 1000pcs/real
Technical Specifications
| Part Number (P/N SJK) | Frequency | Frequency Tolerance (at 25C) | Load Capacitance (CL) | Operating Temperature | Storage Temperature | Shunt Capacitance (C0) | Aging @25C (1st year) |
|---|---|---|---|---|---|---|---|
| 6I12000F20UCG | 12.000000MHz | 20 ppm max | 20.0 PF | -40C to +85 C | -40 C to +125 C | 3.0 PF Max | 3 ppm/year Max |
Reliability Test Specification
| Test Item | Test Conditions | Standard Requirements |
|---|---|---|
| Drop | Free fall from 55cm height onto a wooden board, 3 times | Frequency change within 5ppm, resistance change within 15% before and after test |
| Vibration | Frequency: 10~55Hz, Amplitude: 1.5mm, Duration: 2 hours per orientation (X, Y, Z) | Frequency change within 5ppm, resistance change within 15% before and after test |
| Thermal Shock | 25 cycles of high and low temperature in a test chamber. Low temp: -403C for 30 min, High temp: 852C for 30 min. Temp change every 3 min. | Frequency change within 5ppm, resistance change within 15% before and after test |
| Hermeticity | Helium pressure: 50.5Kg/cm, Helium pressurization time: 120 min | Leak rate: 110-9Pa.m3/s |
| Resistance to Soldering Heat | Wave crest temperature: 260C10C, Time: 155 sec | Frequency change within 5ppm, resistance change within 15% before and after test |
| Tinning Test | Temperature: 260C10C, Soaking time: 31 sec | Tinning coverage of pins 90% |
| High Temperature High Humidity | Temperature: 60C2C, Humidity: 90%~95%, Duration: 240 hours | 1. Frequency change within 5ppm, resistance change within 15% before and after test. 2. Product surface should not rust. |
| High Temperature Test | Temperature: 85C2C, Duration: 240 hours | Frequency change within 5ppm, resistance change within 15% before and after test |
| Low Temperature Test | Temperature: -40C2C, Duration: 240 hours | Frequency change within 5ppm, resistance change within 15% before and after test |
| Life Test | Voltage: 5V, Temperature: 25, Duration: 1000 hours | Frequency change within 5ppm, resistance change within 15% before and after test |