Specifications
Voltage Rating:
50V
Capacitance:
2.2uF
Temperature Coefficient:
X7R
Tolerance:
±10%
Mfr. Part #:
CS2012X7R225K500NRE
Package:
0805
Key Attributes
Model Number:
CS2012X7R225K500NRE
Product Description
SAMWHA CAPACITOR CO., LTD. - MULTILAYER CERAMIC CAPACITOR
Product Description: This document details the Multilayer Ceramic Capacitor, Commercial Grade (Thin Layer Large-Capacitance Type), qualified to IEC-60384 standards. These capacitors are primarily designed for use in computer and communication equipment. Applications for industrial equipment, high reliability equipment, and LED equipment may require further consultation with sales representatives or product engineers.
Product Attributes
- Brand: SAMWHA CAPACITOR CO., LTD.
- Product Type: Multilayer Ceramic Capacitor
- Grade: Commercial Grade
- Type: Thin Layer Large-Capacitance Type
- Certifications: IEC-60384 Qualified
- Origin: KOREA
Technical Specifications
| Part Number | Type Designation | Capacitance | Capacitance Tolerance | Dissipation Factor (Max.) | Insulation Resistance (Min.) | Chip Size (L x W x T) mm | Temperature Coefficient | Voltage (DC) | Termination | Packing |
| CS2012X7R225K500NRE | CS2012X7R225K500NRE | 2.2 | 10 % | 12.5 % | 22.7 | 2.00 0.20 x 1.25 0.15 x 1.25 0.15 | X7R (-55 to +125, 15%) | 50V DC | Ni-Sn (Nickel-Tin Plate) | 7" Reel Type |
| Item | Specification | Test Methods and Conditions |
| Operating Temperature Range | X7R: -55 to +125 | |
| Insulation Resistance | 50F min | Applied the rated voltage for 2 minutes of charging. The charge/discharge current is less than 50mA. |
| Voltage proof | X7R: The rated voltage 250% - Applied between the terminations for 1 to 5 seconds. | The charge/discharge current is less than 50mA. |
| Capacitance | Within the specified tolerance | Measured at 25, 1 0.1kHz, 1 0.2Vrms (for C10) |
| Dissipation Factor | X7R: 12.5%max | |
| Solderability | 95% of the terminations is to be soldered evenly and continuously. | *Pb-Free type Solder: 96.5Sn-3Ag-0.5Cu, Solder temperature: 2455, Immersion time: 30.1sec, *Pre-Heating: at 80~120 for 10~30sec |
| Resistance to Soldering Heat | Capacitance change: Within 7.5% | Preheat the capacitor at 120 to 150 for 1 minute. Immerse the capacitor in a eutectic solder solution at 2605 for 100.5 seconds. Let sit at room temperature for 242 hours, then measure. |
| Rapid change of temperature | Capacitance Change X7R: Within 7.5% | Perform five cycles according to heat treatments. Let sit at room temperature for 242 hours, then measure. |
| Endurance | Capacitance Change X7R: Within 12.5% | Apply 150% of the rated voltage for 1000+48/-0 hrs at the maximum operating temperature 3. Let sit at room temperature for 242 hours, then measure. |
| Substrate bending test | Capacitance Change X7R: Within 10% | Substrate material: Glass EPOXY Board. Thickness: 1.6. Bending limit: 1mm, Pressurizing speed: 1mm/sec, Holding time: 51sec. |
| Vibration | Capacitance within the specified tolerance | Subjected to simple harmonic motion, 1.5mm amplitude, 10 to 55Hz, for 2 hours in each of 3 mutually perpendicular directions. After soldering and then let sit for 242hr at room temperature. |
| Accelerated damp heat, steady state | Capacitance Change X7R: Within 12.5% | Apply the rated voltage at 402 and 90 to 95%RH for 500+24/-0 hrs. Let sit at room temperature for 242 hours, then measure. |
| Temperature characteristic of capacitance | X7R: Within 15% | Measured after 5 min. at each specified temperature stage. Compared with the 25 value over the temperature ranges (-55 to +125). |