Specifications
Voltage Rating:
25V
Capacitance:
2.2uF
Temperature Coefficient:
-
Tolerance:
±10%
Mfr. Part #:
CS2012X7R225K250NRE
Package:
0805
Key Attributes
Model Number:
CS2012X7R225K250NRE
Product Description
STANDARD NO SW-M-04B MULTILAYER CERAMIC CAPACITOR Commercial Grade
These multilayer ceramic capacitors are designed for use in computer equipment, communication equipment, industrial equipment, high reliability equipment, LED equipment, and more. They offer a wide application range and are suitable for various electronic systems.
Product Attributes
- Brand: SAMWHA CAPACITOR CO.,LTD
- Product Type: Multilayer Ceramic Capacitor (Commercial Grade)
- Origin: Not specified
- Material: Not specified
- Color: Not specified
- Certifications: Not specified
Technical Specifications
| Type Designation | Size Code (mm) | Temperature Coefficient | Capacitance Code (pF) | Capacitance Tolerance | Voltage Code (V DC) | Termination Code | Packing Code | Thickness (mm) |
| CS2012X5R225K500NRE | 2012 (2.0 x 1.25) | X5R (-55 to +85) | 225 (2.2M) | K (10%) | 500 | N (Ni-Sn) | R (7" Reel) | Not specified |
| Item | Specification | Test Methods and Conditions |
| Operating Temperature Range | X7R, X7S, X7T: -55 to +125 X5R: -55 to +85 Y5V: -30 to +85 | - |
| Insulation Resistance | 50 M min | Applied the rated voltage for 2 minutes of charging, The charge/discharge current is less than 50mA. |
| Dielectric Strength | No defects or abnormalities | X7R, X7S, X7T, X5R, Y5V: The rated voltage 250% - Applied between the terminations for 1 to 5 seconds. - The charge/discharge current is less than 50mA. |
| Capacitance within the specified tolerance | Capacitance/D.F. should be measured at 25 at the frequency and voltage shown in the table. | C 10F: 1 0.1kHz, 0.5~1.0Vrms C > 10F: 120 24Hz, 0.50.1Vrms |
| Dissipation Factor | X7R, X7S, X7T, X5R: 12.5%max *3216 Size 100F: 15% max Y5V: 20%max | - |
| Solderability of Termination | Termination should be covered with more than 75% of new solder | *Pb-Free type Solder: 96.5Sn-3Ag-0.5Cu Solder temperature: 2455 Immersion time: 30.1sec *Pre-Heating: at 80~120 for 10~30sec |
| Resistance to Soldering Heat | Appearance: No defects which may affect performance Capacitance change: X7R, X7S, X7T, X5R: Within 7.5% Y5V: Within 20% Dissipation Factor: X7R, X7S, X7T, X5R: 12.5%max *3216 Size 100F: 15% max Y5V: 20%max I.R: 50 M min | Preheat the capacitor at 120 to 150 for 1 minute. (Preheating for 3225,4520,4532 Step1:100 to 120, 1min Step2:170 to 200, 1min) Immerse the capacitor in a eutectic solder solution at 2605 for 100.5 seconds. Initial measurement Measurement after test: Let sit at room temperature for 242 hours, then measure. |
| Temperature Cycle | Appearance: No defects which may affect performance Capacitance Change: X7R, X7S, X7T, X5R: Within 7.5% Y5V: Within 20% Dissipation Factor: X7R, X7S, X7T, X5R: 12.5%max *3216 Size 100F: 15% max Y5V: 20%max I.R: 50 M min | Perform the five cycles according to the four heat treatments listed in the following table. Step | Temp () | Min. (min) 1 | Min. operating temp. +0/-3 | 303 2 | Room Temp | 2 to3 3 | Max. operating temp. +3/-0 | 303 4 | Room Temp | 2 to3 Initial measurement Measurement after test: Perform the final measurement according to Note2 |
| High Temperature Load | Appearance: No defects which may affect performance Capacitance Change: X7R, X7S, X7T, X5R: Within 12.5% Y5V: Within 30% Dissipation Factor: X7R, X7S, X7T, X5R: 20%max *3216 Size 100F: 30% max Y5V: 40%max I.R: 12.5 M min | Apply 150% of the rated voltage for 1000+48/-0 hrs at the maximum operating temperature 3. The charge/discharge current is less than 50mA. -Initial measurement -Measurement after test |
| Bending strength | Appearance: No cracking or marking defects shall occur Capacitance Change: X7R, X7S, X7T, X5R: Within 12.5% Y5V: Within 30% Within +30/-40% (cap 10F) | Substrate material: Glass EPOXY Board. Thickness: 1.6 0.8 mm (0603/1005size) * Test condition - Bending limit: 1mm - Pressurizing speed: 1mm/sec - Holding time: 51sec |
| Vibration Resistance | Appearance: No defects or abnormalities Capacitance: Within the specified tolerance Dissipation Factor: X7R, X7S, X7T, X5R: 12.5%max *3216 Size 100F: 15% max Y5V: 20%max | After soldering and then let sit for 242hr at room temperature. The capacitor should be subjected to a simple harmonic motion having a total amplitude of 1.5mm, the frequency being varied uniformly between the approximate limits of 10 and 55Hz, shall be traversed(from 10Hz to 55Hz then 10Hz again) in approximately 1 minute. This motion shall be applied for a period of 2 hours in each 3 mutually perpendicular directions(total is 6 hours). |
| Humidity Load | Appearance: No defects which may affect performance Capacitance Change: X7R, X7S, X7T, X5R: Within 12.5% Y5V: Within 30% Dissipation Factor: X7R, X7S, X7T, X5R: 20%max *3216 Size 100F: 30% max Y5V: 40%max I.R: 12.5 M min | Apply the rated voltage at 402 and 90 to 95%RH for 500+24/-0 hrs. The charge/discharge current is less than 50mA. Initial measurement Measurement after test |
2410121820_SAMWHA-CS2012X7R225K250NRE_C513773.pdf