Specifications
Voltage Rating:
10V
Capacitance:
10uF
Temperature Coefficient:
X5R
Tolerance:
±20%
Mfr. Part #:
GRM188R61A106ME69D
Package:
0603
Key Attributes
Model Number:
GRM188R61A106ME69D
Product Description
Product Overview
This product specification applies to Chip Multilayer Ceramic Capacitors for General Electronic equipment. These capacitors are designed for general-purpose use and are suitable for a wide range of electronic devices.
Product Attributes
- Brand: MURATA
- Part Number System: GRM188R61A106ME69
- Size Code: 0603
- Temperature Characteristics: X5R (EIA)
- Nominal Capacitance: 10uF
- Capacitance Tolerance: +/-20%
- Rated Voltage: DC 10 V
- Packaging: Available in 4000 pcs./Reel (W8P4, 180mm Reel) and 10000 pcs./Reel (W8P4, 330mm Reel)
Technical Specifications
| Item | Specification | Test Method (Ref. Standard:JIS C 5101, IEC60384) | Step | Temperature(C) | Time (min) |
| Rated Voltage | DC 10 V | Shown in Rated value. The rated voltage is defined as the maximum voltage which may be applied continuously to the capacitor. When AC voltage is superimposed on DC voltage, VP-P or VO-P, whichever is larger, should be maintained within the rated voltage range. | |||
| Appearance | No defects or abnormalities. | Visual inspection. | |||
| Dimension | 0603 (L/W: 1.6 +/-0.15, T: 0.8 +/-0.15) | Shown in Rated value. Using Measuring instrument of dimension. | |||
| Voltage Proof | No defects or abnormalities. | Measurement Point : Between the terminations Test Voltage : 250% of the rated voltage Applied Time : 1s to 5s Charge/Discharge Current : 50mA max. | |||
| Insulation Resistance(I.R.) | More than 50F | Measurement Temperature:Room Temperature Measurement Point : Between the terminations Measurement Voltage : Rated Voltage Charging Time : 1min Charge/Discharge Current : 50mA max. | |||
| Capacitance | 10uF +/-20% | Measurement Temperature:Room Temperature Measurement Frequency : 1.0+/-0.1kHz Measurement Voltage : 0.5+/-0.1Vrms | |||
| Q or Dissipation Factor (D.F.) | DF:0.1 max. | Measurement Temperature : Room Temperature Measurement Frequency : 1.0+/-0.1kHz Measurement Voltage : 0.5+/-0.1Vrms | |||
| Capacitance Change (Temperature Characteristics) | +/-20% (within -55 to 85 ) | No bias Within +/-15% The capacitance change should be measured after 5 minutes at each specified temperature stage. Measurement Voltage : Less than 1.0Vrms Pre-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. | 1 Reference Temp. | 25 +/-2 | 2 to 3 |
| 2 Min. Operating Temp. | -55 +/-3 | 30+/-3 | |||
| 3 Reference Temp. | 25 +/-2 | 2 to 3 | |||
| 4 Max. Operating Temp. | 85 +/-3 | 30+/-3 | |||
| 5 Reference Temp. | 25 +/-2 | 2 to 3 | |||
| Adhesive Strength of Termination | No removal of the terminations or other defect should occur. | Solder the capacitor on the test substrate shown in Fig.3. Termination Applied Force : 5N Holding Time : 10+/-1 Applied Direction : In parallel with the test substrate and vertical with the capacitor side | |||
| Vibration | Appearance: No defects or abnormalities. Capacitance: Within the specified initial value. Q or D.F.: Within the specified initial value. | Solder the capacitor on the test substrate shown in Fig.3. Kind of Vibration : A simple harmonic motion 10Hz to 55Hz to 10Hz Vibration Time : 1min Total Amplitude : 1.5mm This motion should be applied for a period of 2hours in each 3 mutually perpendicular directions(total of 6hours). | |||
| Substrate Bending Test | Appearance: No defects or abnormalities. Capacitance: Within +/-10% | Solder the capacitor on the test substrate shown in Fig.1. Pressurization Method : Shown in Fig.2. Flexure : 1mm Change Holding Time : 5+/-1s Soldering Method : Reflow soldering | |||
| Solderability | 95% of the terminations is to be soldered evenly and continuously. | Test Method : Solder bath method Flux : Solution of rosin ethanol 25(mass)% Preheat : 80 to 12010s to 30s Solder : Sn-3.0Ag-0.5Cu(Lead Free Solder) Test Temp. : 245+/-5 Test Time : 2+/-0.5s | |||
| Resistance to Soldering Heat | Appearance: No defects or abnormalities. Capacitance: Within +/-12.5% Q or D.F.: Within the specified initial value. I.R.: Within the specified initial value. Voltage Proof: No defects. | Test Method : Solder bath method Solder : Sn-3.0Ag-0.5Cu(Lead Free Solder) Solder Temp. : 270+/-5 Test Time : 10+/-0.5s Preheat Temp. : 120 to 150 Preheat Time : 1min Post-treatment : Let sit for 24+/-2hours at room temperature, then measure. | |||
| Temperature Sudden Change | Appearance: No defects or abnormalities. Capacitance: Within +/-7.5% Change Q or D.F.: Within the specified initial value. I.R.: Within the specified initial value. Voltage Proof: No defects. | Solder the capacitor on the test substrate shown in Fig.3. Cycles : 5 cycles Pre-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. Post-treatment : Let sit for 24+/-2hours at room temperature, then measure. | 1 Min.Operating Temp. | -55 +0/-3 | 30+/-3 |
| 2 Reference Temp. | 25 +/-2 | 2 to 3 | |||
| 3 Max.Operating Temp. | 85 +3/-0 | 30+/-3 | |||
| 4 Reference Temp. | 25 +/-2 | 2 to 3 | |||
| High Temperature High Humidity (Steady) | Appearance: No defects or abnormalities. Capacitance: Within +/-12.5% Change Q or D.F.: DF:0.2 max. I.R.: More than 500M or 12.5F (Whichever is smaller) | Solder the capacitor on the test substrate shown in Fig.3. Test Temperature : 40+/-2 Test Humidity : 90%RH to 95%RH (Steady) Test Time : 500+/-12h Test Voltage : Rated Voltage Charge/Discharge Current : 50mA max. Pre-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. Post-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. | |||
| Durability | Appearance: No defects or abnormalities. Capacitance: Within +/-12.5% Change Q or D.F.: DF:0.2 max. I.R.: More than 1000M or 25F (Whichever is smaller) | Solder the capacitor on the test substrate shown in Fig.3. Test Temperature : Maximum Operating Temperature+/-3 Test Time : 1000+/-12h Test Voltage : 100% of the rated voltage Charge/Discharge Current : 50mA max. Pre-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. Post-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. |