Specifications
Voltage Rating:
35V
Capacitance:
10uF
Temperature Coefficient:
X5R
Tolerance:
±10%
Mfr. Part #:
GRM21BR6YA106KE43L
Package:
0805
Key Attributes
Model Number:
GRM21BR6YA106KE43L
Product Description
Product Overview
Chip Multilayer Ceramic Capacitors for General Electronic equipment. These capacitors offer reliable performance for general-purpose applications.
Product Attributes
- Brand: MURATA
Technical Specifications
| Part Number | Size Code | Temperature Characteristics | Rated Voltage | Nominal Capacitance | Capacitance Tolerance | Packaging Code | Packaging Unit | Dimensions (L x W x T) (mm) |
| GRM21BR6YA106KE43_ | 0805 | X5R (EIA) | DC 35 V | 10uF | +/-10 % | L | 3000 pcs./Reel (180mm Reel Plastic Tape) | 2.0 x 1.25 x 0.7 (max.) |
| GRM21BR6YA106KE43_ | 0805 | X5R (EIA) | DC 35 V | 10uF | +/-10 % | K | 10000 pcs./Reel (330mm Reel Plastic Tape) | 2.0 x 1.25 x 0.7 (max.) |
Specifications and Test Methods
| Item | Specification | Test Method (Ref. Standard:JIS C 5101, IEC60384) |
| Rated Voltage | Shown in Rated value. The rated voltage is defined as the maximum voltage which may be applied continuously to the capacitor. When AC voltage is superimposed on DC voltage, VP-P or VO-P, whichever is larger, should be maintained within the rated voltage range. | |
| Appearance | No defects or abnormalities. | Visual inspection. |
| Dimension | Shown in Rated value. | Using Measuring instrument of dimension. |
| Voltage Proof | No defects or abnormalities. | Measurement Point : Between the terminations Test Voltage : 250% of the rated voltage Applied Time : 1s to 5s Charge/Discharge Current : 50mA max. |
| Insulation Resistance(I.R.) | More than 50F | Measurement Temperature:Room Temperature Measurement Point : Between the terminations Measurement Voltage : Rated Voltage Charging Time : 1min Charge/Discharge Current : 50mA max. |
| Capacitance | Shown in Rated value. | Measurement Temperature:Room Temperature Measurement Frequency : 1.0+/-0.1kHz Measurement Voltage : 1.0+/-0.2Vrms |
| Q or Dissipation Factor (D.F.) | DF:0.1 max. | Measurement Temperature : Room Temperature Measurement Frequency : 1.0+/-0.1kHz Measurement Voltage : 1.0+/-0.2Vrms |
| Capacitance (Temperature Characteristics) | Within +/-15% | Measurement Temperature:Room Temperature Measurement Voltage : Less than 1.0Vrms (Refer to the individual data sheet) Pre-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. Step Temperature(C) 1 Reference Temp. +/-2 2 Min. Operating Temp. +/-3 3 * Reference Temp. +/-2 4 Max. Operating Temp. 3 5 Reference Temp. +/-2 Applying Voltage No bias |
| Adhesive Strength of Termination | No removal of the terminations or other defect should occur. | Solder the capacitor on the test substrate shown in Fig.3. Termination Applied Force : 10N Holding Time : 10+/-1 Applied Direction : In parallel with the test substrate and vertical with the capacitor side |
| Vibration | Appearance: No defects or abnormalities. Capacitance: Within the specified initial value. Q or D.F.: Within the specified initial value. | Solder the capacitor on the test substrate shown in Fig.3. Kind of Vibration : A simple harmonic motion 10Hz to 55Hz to 10Hz Vibration Time : 1min Total Amplitude : 1.5mm This motion should be applied for a period of 2hours in each 3 mutually perpendicular directions(total of 6hours). |
| Substrate Bending Test | Appearance: No defects or abnormalities. Capacitance: Within +/-10% | Solder the capacitor on the test substrate shown in Fig.1. Pressurization Method : Shown in Fig.2. Flexure : 1mm Change Holding Time : 5+/-1s Soldering Method : Reflow soldering |
| Solderability | 95% of the terminations is to be soldered evenly and continuously. | Test Method : Solder bath method Flux : Solution of rosin ethanol 25(mass)% Preheat : 80 to 12010s to 30s Solder : Sn-3.0Ag-0.5Cu(Lead Free Solder) Test Temp. : 245+/-5 Test Time : 2+/-0.5s |
| Resistance to Soldering | Appearance: No defects or abnormalities. Capacitance: Within +/-15% Q or D.F.: Within the specified initial value. | Test Method : Solder bath method Solder : Sn-3.0Ag-0.5Cu(Lead Free Solder) Solder Temp. : 270+/-5 Test Time : 10+/-0.5s Preheat Temp. : 120 to 150 Preheat Time : 1min Pre-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. Post-treatment : Let sit for 24+/-2hours at room temperature, then measure. |
| Temperature Sudden Change | Appearance: No defects or abnormalities. Capacitance: Within +/-7.5% Q or D.F.: Within the specified initial value. Voltage Proof: No defects. | Test Method : Solder bath method Solder : Sn-3.0Ag-0.5Cu(Lead Free Solder) Solder Temp. : 270+/-5 Test Time : 10+/-0.5s Preheat Temp. : 120 to 150 Preheat Time : 1min I.R. : Within the specified initial value. Pre-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. Post-treatment : Let sit for 24+/-2hours at room temperature, then measure. Step Temperature() 1 Min.Operating Temp. +0/-3 (30+/-3 min) 2 Reference Temp. (2 to 3 min) 3 Max.Operating Temp. +3/-0 (30+/-3 min) 4 Reference Temp. (2 to 3 min) |
| High Temperature High Humidity (Steady) | Appearance: No defects or abnormalities. Capacitance: Within +/-12.5% Q or D.F.: DF:0.2 max. I.R.: More than 500M or 12.5F (Whichever is smaller) | Test Temperature : 40+/-2 Test Humidity : 90%RH to 95%RH (Steady) Test Time : 500+/-12h Test Voltage : Rated Voltage Charge/Discharge Current : 50mA max. Pre-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. Post-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. |
| Durability | Appearance: No defects or abnormalities. Capacitance: Within +/-12.5% Q or D.F.: DF:0.2 max. I.R.: More than 1000M or 25F (Whichever is smaller) | Test Temperature : Maximum Operating Temperature+/-3 Test Time : 1000+/-12h Test Voltage : 100% of the rated voltage Charge/Discharge Current : 50mA max. Pre-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. Post-treatment : Perform a heat treatment at 150+0/-10C for 1hour and then let sit for 24+/-2hours at room temperature, then measure. |
2410121856_muRata-GRM21BR6YA106KE43L_C162422.pdf
Request A Quote