Specifications
Normal temperature Frequency Tolerance:
±30ppm
Frequency Stability:
±20ppm
Operating Temperature:
-20℃~+70℃
Load Capacitance:
20pF
Equivalent Series Resistance(ESR):
40Ω
Frequency:
24MHz
Mfr. Part #:
KUS240002030
Package:
HC-49S
Key Attributes
Model Number:
KUS240002030
Product Description
Product Overview
The KYX 49US/24.000MHZ is a Quartz Crystal Resonator manufactured by Shenzhen Kaiyuexiang Electronics Co., Ltd. It is designed for oscillation and features a frequency of 24.000 MHz with a frequency tolerance of 30ppm and a load capacitance of 20pF.
Product Attributes
- Brand: Kaiyuexiang
- Origin: Shenzhen, China
- Product Name: Quartz Crystal Resonator
- Product Model: 49US/24.000MHZ
- Original Manufacturer Model: KUS240002030
Technical Specifications
| Parameter | Value |
|---|---|
| Holder Type | 49US |
| Mode of Vibration | AT CUT |
| Oscillation Mode | FUND S&A |
| Test Facilities | KH-1240 |
| Storage Temperature | -40 TO +85 |
| Driver Level | 100W |
| Normal Frequency | 24.000 MHz |
| Frequency Tolerance (252) | 30ppm |
| Temperature Stability | 20ppm |
| Operating Temperature Range | -20 TO +70 |
| Load Capacitance | 20 PF |
| Motional Capacitance | 5PF MAX |
| Shunt Capacitance | 40 MAX |
| Effective Series Resistance | 500M OHMS MIN AT DC 100V |
| Insulation Resistance | 95% COVERAGE BY USING 90/10 SOLD AT 245FOR 5 SEC. DIPING AFTER IMMERSION IN ALPHA 611 FLUX FOR 5 SEC. |
| Solderability | 95% COVERAGE BY USING 90/10 SOLD AT 245FOR 5 SEC. DIPING AFTER IMMERSION IN ALPHA 611 FLUX FOR 5 SEC. |
| Shock Test | Electrical characteristics shall be satisfied after dropping three times from the height of 50 cm onto Hard wooden board. |
| Vibration Test | Electrical characteristics shall be satisfied after supplying Vibration: Frequency 1055Hz, Period 12min, Full Amplitude 1.5mm P-P, Direction X.Y.Z, Time 2 hours/each direction. |
| Strength of Terminals/Lead-wires (Pulling) | Body of specimen shall be fixed, and 900g of tension weight shall be supplied gradually to axial direction of terminals/lead-wires for 30 sec. No visual damages after test. |
| Strength of Terminals/Lead-wires (Bending) | Body of specimen shall be fixed, and 90degree bending shall be given, being supplied 225gs tension weight. Then straightened gradually. Same bending and straightening to the opposite direction. No visual damages after test. |
| Sealing Tightness | No observation of gas bubble after specimen put in hot water at +90+95 for 5 min. |
| Soldering Dip | Terminals/lead-wires of specimen shall be dipped into solder melted tank at +2305 for 3sec. Dipping depth shall be 2mm from the bottom of specimens body. Soldering portion shall be covered in over 90% of terminals/lead-wires dipped. |
| Solder Heating | Terminals/lead-wires of specimen shall be dipped into solder melted tank at +35010 for 3-4 sec. Electrical characteristics shall be satisfied after dipping depth shall be 2mm from edge of terminals/lead-wires. |
| Humidity Test | Electrical characteristics shall be satisfied after letting it alone at 602 in humidity of 9095% for 250 hours. |
| Storage in Low Temperature | Electrical characteristics shall be satisfied after letting it alone at -302 for 250 hours. |
| Storage in High Temperature | Electrical characteristics shall be satisfied after letting it alone at +852 for 250 hours. |
| Temperature Cycle | Electrical characteristics shall be satisfied after supplying the following temperature cycle (3 cycles). Temperature shift from low to high, high to low shall be done in 1/min. |