Specifications
Voltage Rating:
50V
Capacitance:
100nF
Temperature Coefficient:
X7R
Tolerance:
±10%
Pin Spacing:
2.54mm
Mfr. Part #:
178MU0006
Package:
Through Hole,P=2.54mm
Key Attributes
Model Number:
178MU0006
Product Description
Product Overview
The CT40805B104K500C1 is a radial leaded MLCC (Multi-Layer Ceramic Capacitor) designed for automatic placement with tape and reel packaging. It features a miniature size with large capacitance, epoxy resin coating for excellent moisture resistance, mechanical strength, and heat resistance. This product is manufactured to industrial production standard sizes and offers various lead configurations, making it suitable for general-purpose applications.
Product Attributes
- Product Type: Radial Leaded MLCC
- Packaging: Bulk ()
Technical Specifications
| Product Model | Nominal Capacitance | Tolerance | Rated Voltage | Dielectric | Body Size (L x W) | Pitch (P) | Leads Type | Packaging Code |
|---|---|---|---|---|---|---|---|---|
| CT40805B104K500C1 | 104 (100,000pF) | 10% | 50V | X7R | 0805 (0.17 x 0.15 inches) | 2.54mm | B1 | C1 |
| Detailed Specifications: | ||||||||
| Parameter | Class I (NPO) | Class II (X7R) | Class II (X5R) | Class II (Y5V) | Test Frequency | Test Voltage | Remarks | |
| Capacitance | Within specified tolerance | Within specified tolerance | Within specified tolerance | +80% ~ -20% | 1MHz 10% (1000pF), 1kHz 10% (>1000pF) | 1.0V | Pre-treatment required for Class II | |
| Dissipation Factor (DF) | 0.15% (CR50pF) | 3.5% | 3.5% | 7.5% (CR0.1uF), 15% (0.1uFCR1uF), 17.5% (CR1uF) | 1kHz 10% | 1.0V (Class II, B), 0.3V (Class II, Y) | ||
| Insulation Resistance | 10000M (C10nF), 100MuF (C10nF) | 4000M (C25nF), 100MuF (C25nF) | Rated Voltage | Duration: 605s | ||||
| Withstanding Voltage | 300% Rated Voltage | 250% Rated Voltage | Between terminals: Duration: 51s. Between terminals and body: 2.5UR, Duration: 1~5s. Charge/discharge current 50mA. | |||||
| Solder Ability | Lead wire 95% covered with new solder coating. Dipping in 25% rosin alcohol solution, then molten solder at 2305 for 20.5s. | |||||||
| Resistance to Soldering Heat | Capacitance change: 2.5% or 0.25pF (whichever is larger). Recovery: 4-24 hours (Class I). Preconditioning: 150+0/-10 for 1 hour, then 484 hours recovery (Class II). | Capacitance change: 10% (X7R), 20% (X5R). Recovery: 484 hours. | Capacitance change: 20% (X5R). Recovery: 484 hours. | Capacitance change: +80% ~ -20%. Recovery: 484 hours. | Solder temperature: 2605. Duration: 10 1s. | |||
| Terminal Strength (Tensile) | No visible breakage or looseness. Apply force up to 10N along lead direction, hold for 101 seconds. | |||||||
| Bending Strength | Apply 0.25Kg force, bend 90 degrees for 5s, return to original position. Repeat 2 cycles. | |||||||
| Temperature Cycle | Capacitance change: 5% or 0.5pF (whichever is larger). DF: < 2x initial value. Recovery: 1 hour (Class I). Preconditioning: 150+0/-10 for 1 hour, then 484 hours recovery (Class II). | Capacitance change: 12.5%. DF: 5.0% (CR0.1uF), 15.0% (0.1uFCR1uF), 17.5% (CR0.1uF). | Capacitance change: 12.5%. DF: 5.0% (CR0.1uF), 15.0% (0.1uFCR1uF), 17.5% (CR0.1uF). | Capacitance change: 30%. DF: 12.5% (CR0.1uF), 15.0% (0.1uFCR1uF), 17.5% (CR0.1uF). | Steps: Room Temp (2-3min), -55 (30min), Room Temp (2-3min), 125 (30min), Room Temp (2-3min). Cycle count: 5. | Insulation Resistance: 1000M or 50MuF (whichever is smaller). | ||
| High Temperature Loading Test | Capacitance change: 3% or 0.3pF (whichever is larger). DF: < 2x initial value. Recovery: 242 hours (Class I). | Capacitance change: 12.5%. DF: 5.0% (CR0.1uF), 15.0% (0.1uFCR1uF), 17.5% (CR0.1uF). Recovery: 484 hours (Class II). | Capacitance change: 12.5%. DF: 5.0% (CR0.1uF), 15.0% (0.1uFCR1uF), 17.5% (CR0.1uF). Recovery: 484 hours. | Capacitance change: 30%. DF: 12.5% (CR0.1uF), 15.0% (0.1uFCR1uF), 17.5% (CR0.1uF). Recovery: 484 hours. | Temperature: 125 (Class I), 85 (Class II). Applied voltage: 1.5x rated voltage. Duration: 1000+48/-0 hours. | Insulation Resistance: 500M or 25MuF (whichever is smaller). | ||
| Solvent Resistance | No defects or abnormalities in appearance, legible marking. Immerse in solvent at 235 for 1 min, brush notation area 10 times with cotton, repeat 3 times. | |||||||
Standard Conditions: Temperature: 5~35, Relative Humidity: 45~85%, Atmospheric Pressure: 86~106kPa.
Arbitration Test Conditions: Temperature: 251, Relative Humidity: 48%~52%, Atmospheric Pressure: 86~106kPa.