Specifications
Voltage Rating:
25V
Capacitance:
1uF
Temperature Coefficient:
X6S
Tolerance:
±10%
Mfr. Part #:
C0402S105K025TOF
Package:
0402
Key Attributes
Model Number:
C0402S105K025TOF
Product Description
Product Overview
The NCC-023-2005 Multilayer Ceramic Chip Capacitor (MLCC) is designed for general electric circuits, telecommunications, personal computers and peripherals, power circuits, and mobile applications. This series is compliant with RoHS & HF standards and operates within a voltage range of 4V to 50V.
Product Attributes
- Brand: Holy Stone Enterprise Co., Ltd
- Trademark: IHHEC
- Certifications: RoHS, HF
Technical Specifications
| Item | Specification | Test Condition |
| Visual | No abnormal exterior appearance | Visual Inspection |
| Dimension | See Page 2 | Visual Inspection |
| Insulation Resistance | 500/C min. | Applied Voltage: Rated Voltage Charge Time : 605 sec. Charge-Discharge current shall be less than 50mA current. |
| Capacitance | Within The Specified Tolerance | Class |
| D.F. | Class X6S: 10% max. | Char Frequency Voltage X6S 1KHz10% 1.00.2Vrms or 0.50.2Vrms |
| Withstanding Voltage | No dielectric breakdown or mechanical breakdown | 250% of the rated voltage for 1~5 sec. charge/discharge Current is less than 50mA. |
| Temperature Capacitance Coefficient | Class : C1:Capacitance At Standard Temperature(25) C2: Capacitance At Test Temperature (T2) under 1.0Vrms. | X6S -55~+105 22% |
| Adhesive Strength Of Termination | No indication of peeling shall occur on the terminal electrode. | Pull force shall be applied for 10 1 second. 0201----2N( 0.2 Kgf) 0402/0603----5N( 0.5 Kgf) 0805----10N(1.0 Kgf) |
| Resistance to Flexure of Substrate | Appearance: No mechanical damage or capacitance change more than the following table. | The board shall be bend 1.0mm with a rate of 1.0 mm/sec. The duration of the applied forces shall be 5 1sec C-Meter Capacitance Change Char. Cap. Change X6S (S) 12.5% of initial value C2C1 100% C1 R230 C Meter 451mm 451mm Bending Limit Nf |
| Solderability | More than 90% of the terminal surface is to be soldered newly, so metal part does not come out or dissolve. | Solder Temperature : 245 5 Dip Time : 5 0.5sec Immersing Speed : 2510% mm/s Solder : Lead Free Solder Flux :Rosin Preheat : At 80~120 for 10~30sec. |
| Resistance To Soldering Heat | Appearance: No mechanical damage shall occur. Class capacitor shall be set for 484 hours at room temperature after one hour heat treatment at 150 +0/-10 before initial measure. | Preheat : at 150 10 for 60~120sec. Dip : solder temperature of 260 5 Dip Time : 10 1sec. Immersing Speed : 2510% mm/s Flux :Rosin Measure at room temperature after cooling for Class: 48 4 Hours Capacit-ance Class X6S 7.5% of initial value D.F. Class X6S: 10% max. Insulation Resistance To satisfy the specified initial value |
| Temperature Cycle | Appearance: No mechanical damage shall occur. Class capacitor shall be set for 484 hours at room temperature after one hour heat treatment at 150 +0/-10 before initial measure. Capacitor shall be subjected to five cycles of the temperature cycle as following: Measure at room temperature after cooling for Class: 48 4 Hours | Step Temp.() Time(min) 1 Min Rated Temp. +0/-3 30 2 25 3 3 Max Rated Temp. +3/-0 30 4 25 3 Capacit-ance Class X6S 10.0% of initial value D.F. Class X6S: 10% max. Insulation Resistance To satisfy the specified initial value |
| Humidity | Appearance: No mechanical damage shall occur. Class capacitor shall be set for 48 4 hours at room temperature after one hour heat treatment at 150 +0/-10 before initial measure. | Temperature : 40 2 Relative Humidity : 90 ~ 95%RH Test Time : 500 Hrs Max. Measure at room temperature after cooling for Class: 48 4 Hours Capacit-ance Characteristic Cap. Change X6S 12.5% of initial value D.F. Class X6S: 20% max. Insulation Resistance 50/C min. |
| Humidity Load | Appearance: No mechanical damage shall occur. Class capacitors applied DC voltage of the rated voltage is applied for one hour at maximum operation temperature then shall be set for 48 4 hours at room temperature and the initial measurement shall be conducted. | Applied Voltage :Rated Voltage Temperature : 40 2 Relative Humidity : 90 ~ 95%RH Test Time : 500 Hrs Max. Current Applied : 50 mA Max. Class capacitor for Cap103(10nF) shall be set for 242 hours at room temperature after one hour heat treatment at 150 +0/-10 before final measure. Class capacitor for Cap103(10nF) Measure at room temperature after cooling for 48 4 Hours. Capacit-ance Characteristic Cap. Change X6S 12.5% of initial value D.F. Class X6S: 20% max. Insulation Resistance 25/C min. |
| High Temperature Load (Life Test) | Appearance: No mechanical damage shall occur. The capacitors applied DC testing voltage is applied for one hour at maximum operation temperature then shell be set for 48 4 hours at room temperature and the initial measurement shall be conducted. | Applied Voltage: Rated Voltage Temperature: max. operation temperature Test Time : 1000 Hrs Max. Current Applied : 50mA Max Class capacitor for Cap103(10nF) shall be set for 242 hours at room temperature after one hour heat treatment at 150 +0/-10 before final measure. Class capacitor for Cap103(10nF) Measure at room temperature after cooling for 48 4 Hours. Capacit-ance Characteristic Cap. Change X6S 12.5% of initial value D.F. Class X6S: 20% max. Insulation Resistance 50/C min. |
| Vibration | Appearance: No mechanical damage shall occur. Solder the capacitor on P.C. board. | Vibrate the capacitor with amplitude of 1.5mm P-P changing the frequencies from 10Hz to 55Hz and back to 10Hz in about 1 min. Repeat this for 2 hours each in 3 perpendicular directions. Capacit-ance Within the specified tolerance D.F. Class To satisfy the specified initial value Insulation Resistance To satisfy the specified initial value |