Specifications
Voltage Rating:
6kV
Capacitance:
3.3nF
Pin Spacing:
12.5mm
Mfr. Part #:
HVC-6KV-D20-F12.5-332K
Package:
Through Hole,P=12.5mm
Key Attributes
Model Number:
HVC-6KV-D20-F12.5-332K
Product Description
Product Overview
High Voltage Ceramic Capacitor (Ceramic Disc Capacitor) designed for high voltage electric equipment. Features include excellent temperature characteristics and reliability, suitable for demanding applications.
Product Attributes
- Brand: HVC Capacitor
- Origin: China (Manufacturing base in Dongguan Humen)
- Material: High voltage ceramic, N4700 military-grade ceramic dielectric material
- Color: Blue ceramic disc type, Black epoxy resin encapsulation for bolt type
- Certifications: Not explicitly mentioned, but implies high reliability for demanding industries.
Technical Specifications
| Part Number | Temperature Characteristic | Capacitance (pF) | Capacitance Tolerance (%) | DC Rated Voltage (kV) | Dimensions (mm) (D x T x F) | Lead Style | Packing Type | Pack Qty. |
|---|---|---|---|---|---|---|---|---|
| HVC-6KV-D20-F12.5-332K | Y5T | 3300 | ±10 | 6 | 20 x 12.5 x 12.5 | Straight long | Bulk | 500 |
| Test Item | Specification | Testing Method |
|---|---|---|
| Appearance | Dimensions as per 3,4. | Visual examination or Vernier Calipers. |
| Marking | To be easily legible. | Visual examination. |
| Dielectric Strength (Between Lead wires) | No failure (150% of rated voltage for 60s). | DC voltage applied in insulating liquid or gas (Charge/discharge current: 50mA max.). |
| Body insulation | No failure (15kV for 10s). | DC voltage applied between lead wires and small metals (Charge/discharge current: 50mA max.). |
| Insulation Resistance (I.R.) | 100,000 MΩ min. | Measured with DC 1kV within 60±5s of charging. |
| Capacitance | Within specified tolerance. | Measured at 20°C with 1±0.2kHz and AC5V(r.m.s.) max. |
| Dissipation Factor (D.F.) | 0.2% max. | Same condition as capacitance measurement. |
| Temperature Characteristic (Capacitance Change) | Y5T: +22.0%~-33.0% | Capacitance measured at different temperatures (20°C, 85°C). |
| Strength of Lead Pull | Lead wire shall not cut off. Capacitor shall not be broken. | Tensile weight up to 10N applied for 10±1 s in radial direction. |
| Bending | Each lead wire shall be subjected to 5N weight and then a 90° to bend, in one direction, return to original position, and then a 90° bend in the opposite direction. | Rate of one bend in 2 to 3 s. |
| Solderability of Leads | Lead wire shall be soldered with uniformly coated on the axial direction over 3/4 of the circumferential direction. | Dipped into 25% methanol solution of rosin then molten solder of 235±5°C for 2±0.5 s. Dipping depth: 1.5 to 2.0mm from lead root. |
| Soldering Effect (Appearance) | No marked defect. | Lead wires immersed into melted solder of 350±10°C for 3.5±0.5 s. Stored for 24±2 h at room condition. |
| Soldering Effect (Capacitance Change) | Within ±10% | Measured after soldering effect test. |
| Soldering Effect (Dielectric Strength) | No failure | Measured after soldering effect test. |