Specifications
Voltage Rating:
35V
Capacitance:
4.7uF
Temperature Coefficient:
X5R
Tolerance:
±10%
Mfr. Part #:
CGA0603X5R475K350JT
Package:
0603
Key Attributes
Model Number:
CGA0603X5R475K350JT
Product Description
Product Overview
The CGA0603X5R475K350JT is a multilayer ceramic capacitor (MLCC) with an X5R dielectric. It offers a capacitance of 4.7F and a rated voltage of 35Vdc. This capacitor is designed for general-purpose applications and is supplied in tape and reel packaging.
Product Attributes
- Brand: Not specified
- Origin: Not specified
- Material: Ceramic dielectric, Nickel inner electrode, Copper outer electrode
- Color: Not specified
- Certifications: JIS C 5101, IEC60384 (referenced for testing methods)
Technical Specifications
| Part Number | Size (mm) | Dielectric | Capacitance | Tolerance | Rated Voltage | Temperature Characteristic | Packaging |
| CGA0603X5R475K350JT | 1.60 x 0.80 x 0.80 | X5R | 4.7F | 10% | 35Vdc | 15% (-55 to +85) | Tape and Reel (180mm, 4,000 pcs) |
Test Specifications
| Test Item | Specification | Test Method (Reference Standard: JIS C 5101, IEC60384) |
| Appearance | No defects or abnormalities. | Visual (Microscope) inspection. |
| Dimension | Conforms to specifications. | Micrometer measurement. |
| Voltage Proof | Withstand test voltage without defects. | 250% RV for RV50V, 200% RV for 50VRV250V, 150% RV for 250VRV630V, 120% RV for 630VRV1000V. Test time: 1-5s. Max charge/discharge current: 50mA. |
| Insulation Resistance (I.R.) | 100M (for X7R/X5R) | Test temp: 25. Between terminals. Test voltage: 500V: Rated voltage; >500V: 500V. Charge time: 1 minute. Max charge/discharge current: 50mA. |
| Capacitance | Within specified tolerance. | Measurement temp: 25. |
| Q Factor / Dissipation Factor (D.F.) | C10F: 3.5% (C10), 5.0% (10C10), 10% (10C10). C>10F: 15% (C>10). | Frequency: 120Hz24Hz (C10F), 1.00.1 KHz (C>10F). Voltage: 0.5V0.1Vrms (C10F), 1.00.2Vrms (C>10F). |
| Temperature Characteristics of Capacitance | X5R: 15%. X7R: 15%. | Measured at specified temperature stages (-55 to +85) after thermal equilibrium. |
| Adhesive Strength of Termination | No terminal detachment, ceramic breakage. | Welded to test substrate. Applied force: 5N (0402: 2.5N / 0201: 1N). Duration: 101s. |
| Substrate Bending Test | Appearance: No defects. C/C: 10% (General series), 12.5% (High capacitance series). | Soldered on PCB, bent 1mm. |
| Solderability | 95% of terminals uniformly soldered. | Solder: Sn-3.0Ag-0.5Cu. Flux: 25% Rosin in IPA. Temp: 2455C. Time: 20.5s. Immersion: until both ends are fully wetted. |
| Resistance to Soldering Heat | Appearance: No cracks. Capacitance change: 7.5% (X7R/X5R). Q/DF: Same as initial. IR: Same as initial. Voltage Proof: No defects. | Pre-heat: 110-140C, 1 min. Heat treatment: 150+0/-10C for 1 hr, then 242 hrs at room temp. Solder bath: Sn-3.0Ag-0.5Cu, 2605C, 101s. Post-treatment: 242 hrs at room temp. |
| Temperature Cycle | Appearance: No defects. Capacitance change: 7.5% (X7R/X5R). Q/DF: Same as initial. IR: Same as initial. | 5 cycles. -55 to +125. Dwell time: 303 min at temp extremes, 2-5 min at room temp. Pre-treatment and post-treatment as above. |
| High Temperature High Humidity (Load) | Appearance: No defects. Capacitance change: 12.5% (X5R/X7R). Q/DF: 16V: 7% or 2x initial; 25V: 5% or 2x initial. IR: 500M or RC5s. | Test temp: 402. Humidity: 90-95%RH. Test time: 50024 hrs. Test voltage: Rated voltage (630V). Pre-treatment and voltage conditioning as specified. |
| Life Test | Appearance: No defects. Capacitance change: 12.5% (X5R/X7R). Q/DF: 16V: 7% or 2x initial; 25V: 5% or 2x initial. IR: 1G or RC50s. | Test temp: Max operating temp 3. Test time: 100012 hrs. Test voltage: 100% RV. Pre-treatment and voltage conditioning as specified. |