Specifications
Voltage Rating:
10V
Capacitance:
22uF
Temperature Coefficient:
X5R
Tolerance:
±20%
Mfr. Part #:
CGA0603X5R226M100JT
Package:
0603
Key Attributes
Model Number:
CGA0603X5R226M100JT
Product Description
Product Overview
The CGA0603X5R226M100JT is a multilayer ceramic capacitor designed for various electronic applications. It offers a capacitance of 22F with a rated voltage of 10Vdc and features X5R temperature characteristics. This capacitor is supplied in a 0603 package size and is suitable for applications requiring stable capacitance over a range of temperatures.
Product Attributes
- Brand: CGA (implied from product code)
- Material: Dielectric ceramic, Nickel inner electrode, Copper outer electrode, Tin layer
- Packaging: Tape and Reel (180mm diameter), 4,000 pieces per reel
Technical Specifications
| Parameter | Specification | Test Method (Reference Standard: JIS C 5101, IEC60384) |
| Model | CGA0603X5R226M100JT | |
| Dimensions (mm) | Length: 1.600.20, Width: 0.800.20, Thickness: 0.800.20 | Micrometer measurement |
| Temperature Characteristics | X5R, 15% (from -55 to +85) | Measurement at specified temperature stages |
| Capacitance | 22F | 20% tolerance |
| Rated Voltage | 10Vdc | |
| Appearance | No defects or abnormalities. | Visual (microscope) inspection. |
| Voltage Proof | 250% RV (for RV 50V) | 1-5 seconds duration, Max 50mA charging/discharging current |
| Insulation Resistance (I.R.) | 50M (for X7R/X5R) | 25, between terminals, 500V test voltage, 1 minute charge time, Max 50mA charging/discharging current |
| Quality Factor/Dissipation Factor (D.F.) | C 10F: 5.0% (for X7R/X5R) | 120Hz24Hz, 0.5V0.1Vrms |
| Adhesive Strength of Termination | No terminal detachment, ceramic breakage. | 5 N force for 101 sec, applied horizontally. |
| Substrate Bending Test | Appearance: No defects or abnormalities. C/C | Capacitor reflow soldered on PCB, then bent 1 mm. |
| Solderability | 95% of terminals should be uniformly and continuously soldered. | Sn-3.0Ag-0.5Cu solder, 2455C, 20.5s dwell time. |
| Resistance to Soldering Heat | Appearance: No cracks. Capacitance Change: 7.5% (for X7R/X5R). Insulation Resistance: Same as initial. Voltage Proof: No defects or abnormalities. | Pre-heat 110-140C for 1 min. Solder bath 2605C for 101s. |
| Temperature Cycle | Appearance: No defects or abnormalities. Capacitance Change: 7.5% (for X7R/X5R). Insulation Resistance: Same as initial. | 5 cycles: -55 to +150. |
| High Temperature High Humidity (Load) | Appearance: No defects or abnormalities. Capacitance Change: 12.5% (for X5R/X7R). Insulation Resistance: 500M or RC5s (whichever is smaller). | 402, 90%-95%RH for 50024 hours, Rated Voltage applied. |
| Life Test | Appearance: No defects or abnormalities. Capacitance Change: 12.5% (for X5R/X7R). Insulation Resistance: 1G or RC50s (whichever is smaller). | Highest operating temperature for 100012 hours, 100% Rated Voltage applied. |