Specifications
Voltage Rating:
10V
Capacitance:
100uF
Temperature Coefficient:
X5R
Tolerance:
±20%
Mfr. Part #:
CGA1210X5R107M100RT
Package:
1210
Key Attributes
Model Number:
CGA1210X5R107M100RT
Product Description
Product Overview
The CGA1210X5R107M100RT is a multilayer ceramic capacitor designed for various electronic applications. It features X5R temperature characteristics, a capacitance of 100F, and a rated voltage of 10Vdc. This capacitor is suitable for use in demanding environments and applications requiring high reliability.
Product Attributes
- Brand: CGA (implied from part number)
- Temperature Characteristic: X5R
- Capacitance: 100F
- Rated Voltage: 10Vdc
- Tolerance: 20%
- Packaging: Tape & Reel (Plastic Tape)
- Reel Diameter: 180mm (7")
- Packaging Quantity: 1,000 pcs
Technical Specifications
| Item | Specification | Test Method (Ref. Standard: JIS C 5101, IEC60384) |
| Appearance | No defects or abnormalities. | Visual (Microscope) Inspection. |
| Dimensions | Conforms to specifications. | Micrometer inspection of physical dimensions. |
| Voltage Proof | Withstand test voltage without defects or abnormalities. (X7R/X5R, RV50V: 250% RV, Test Time: 1-5s) | Test voltage depends on Rated Voltage (RV). |
| Insulation Resistance (I.R.) | 100M (X7R/X5R, Test Temp: 25, Test Voltage: 500V: RV, >500V: 500V, Charge Time: 1 min) | Between terminals. |
| Capacitance | Within specified tolerance. | Measurement Temp: 25, Frequency: 120Hz24Hz, Voltage: 0.5V0.1Vrms. |
| Q Factor / Dissipation Factor (D.F.) | C10F: 3.5% (1.00.1 KHz, 1.00.2Vrms); 10FC103: 5.0%; 104C103: 10%; C106: 15% (X7R/X5R) | Frequency and voltage vary with capacitance. |
| Temperature Characteristics of Capacitance | X5R: 15%; X7R: 15% | Measurement at various temperature stages (-55 to +85). |
| Adhesive Strength of Termination | No terminal peeling, ceramic breakage, etc. | 5 N force applied for 101s. |
| Substrate Bending Test | Appearance: No defects or abnormalities. C/C | Capacitor soldered on PCB, then bent 1mm. |
| Solderability | 95% of terminals should be uniformly and continuously soldered. | Solder: Sn-3.0Ag-0.5Cu (Lead-free). Flux: Isopropyl alcohol Rosin 25% solid solution. Solder Temp: 2455C, Dwell Time: 20.5s. |
| Resistance to Soldering Heat | Appearance: No cracks. Capacitance Change: X7R/X5R: 7.5%. Q/DF: Same as initial. IR: Same as initial. Voltage Proof: No defects or abnormalities. | Pre-treatment: Heat treatment at 150+0/-10C for 1 hour, then aged. Solder bath method. |
| Temperature Cycle | Appearance: No defects or abnormalities. Capacitance Change: X7R/X5R: 7.5%. Q/DF: Same as initial. IR: Same as initial. | 5 cycles from -55 to +125 (approx.). |
| High Temperature High Humidity (Load) | Appearance: No defects or abnormalities. Capacitance Change: X5R/X7R: 12.5%. Q/DF: 16V: 7% or 2x initial; 25V: 5% or 2x initial. IR: 500M or R.C5s. | Test Temp: 402, Humidity: 90%-95%RH, Test Time: 50024 hours, Test Voltage: Rated voltage. |
| Life Test | Appearance: No defects or abnormalities. Capacitance Change: X5R/X7R: 12.5%. Q/DF: 16V: 7% or 2x initial; 25V: 5% or 2x initial. IR: X5R/X7R: 1G or R.C50s. | Test Temp: Max operating temp 3, Test Time: 100012 hours, Test Voltage: 100% R.V. |