Specifications
Voltage Rating:
10V
Capacitance:
10uF
Temperature Coefficient:
X5R
Tolerance:
±10%
Mfr. Part #:
CGA0603X5R106K100JT
Package:
0603
Key Attributes
Model Number:
CGA0603X5R106K100JT
Product Description
Product Overview
The CGA0603X5R106K100JT is a multilayer ceramic chip capacitor with X5R temperature characteristics. It offers a capacitance of 10F and a rated voltage of 10Vdc. This capacitor is designed for various electronic applications and is supplied in tape and reel packaging.
Product Attributes
- Brand: Not specified
- Origin: Not specified
- Material: Ceramic dielectric, Nickel internal electrode, Copper external electrode
- Color: Not specified
- Certifications: Not specified
Technical Specifications
| Part Number | Size (mm) L*W*T | Temperature Characteristic | Capacitance | Capacitance Tolerance | Rated Voltage | Packaging |
| CGA0603X5R106K100JT | 1.60*0.80*0.80 | X5R | 10F | 10% | 10Vdc | Tape & Reel (180mm reel, 4,000 pcs) |
Specifications and Test Methods
| Test Item | Specification | Test Method (Reference Standard: JIS C 5101, IEC60384) |
| Appearance | No defects or abnormalities. | Visual (microscope) inspection of product. |
| Dimension | Conforms to specifications. | Check physical dimensions of equipment using a micrometer. |
| Voltage Proof | Withstand test voltage without defects or abnormalities. | X7R/X5R: RV50V: 250% RV; 50VRV250V: 200% RV; 250VRV630V: 150% RV; 630VRV1000V: 120% RV. Test time: 1 to 5 seconds. Max charging/discharging current: 50mA. |
| Insulation Resistance (I.R.) | 100M | X7R/X5R. Test temperature: 25. Test points: Between terminals. Test voltage: 500V: Rated voltage; >500V: 500V. Charging time: 1 minute. Max charging/discharging current: 50mA. |
| Capacitance | Within specified tolerance. | Measurement temperature: 25. Material: X5R. Capacitance: 10F. Frequency: 120Hz24Hz. Voltage: 0.5V0.1Vrms. |
| Q Factor / Dissipation Factor (D.F.) | C10F: 10% (X5R); C>10F: 15% (X5R) | Frequency: 120Hz24Hz. Voltage: 0.5V0.1Vrms. |
| Temperature Characteristics of Capacitance | X5R: 15% | Measure capacitance at specified temperature stages after thermal equilibrium. Steps: 1. Reference temp: 252; 2. Min operating temp: -553; 3. Reference temp: 252; 4. Max operating temp: +852; 5. Reference temp: 252. Measurement should be within 5 minutes after thermal equilibrium. |
| Adhesive Strength of Termination | No terminal detachment, ceramic breakage, etc. | Mounting method: Solder capacitor on test substrate. Force: 5 N (0402: 2.5 N / 0201: 1 N). Duration: 101 sec. Application direction: Apply gradual force in horizontal direction along the center of the specimen. |
| Substrate Bending Test | Appearance: No defects or abnormalities. C/C: X5R: 10% | Mount capacitor on PCB, then bend 1 mm. |
| Solderability | 95% of terminals should be uniformly and continuously soldered. | Solder: Sn-3.0Ag-0.5Cu (lead-free). Flux: Isopropyl alcohol Rosin 25% solid solution. Soldering temperature: 2455C. Dwell time: 20.5s. Solder position: Until both ends are completely wetted. |
| Resistance to Soldering Heat | Appearance: No cracks. Capacitance Change: X5R: 7.5%. Q/DF: Same as initial. Insulation Resistance: Same as initial. Voltage Proof: No defects or abnormalities. | Pre-treatment: Heat treatment at 150 +0/-10C for 1 hour, then stand at room temp for 242 hours. Solder bath method. Solder type: Sn-3.0Ag-0.5Cu (Lead Free Solder). Test temperature: 2605C. Test time: 101s. Preheating temperature: 110 to 140. Preheating time: 1 minute. Post-treatment: Stand at room temp for 242 hours. |
| Temperature Cycle | Appearance: No defects or abnormalities. Capacitance Change: X5R: 7.5%. Q/DF: Same as initial. Insulation Resistance: Same as initial. | Mount capacitor on test substrate. Pre-treatment: Heat treatment at 150 +0/-10C for 1 hour, then stand at room temp for 242 hours. Temperature cycle: 5 cycles. Steps: 1. Min temp: -553, 303 min; 2. Room temp: 2~5 min; 3. Max temp: +1253, 303 min; 4. Room temp: 2~5 min. Post-treatment: Stand at room temp for 242 hours. |
| High Temperature High Humidity (Load) | Appearance: No defects or abnormalities. Capacitance Change: X5R: 12.5%. Q/DF: 7% or 2x initial value (for 16V), 5% or 2x initial value (for 25V, take larger). Insulation Resistance: 500M or R.C5s (whichever is smaller). | Mount capacitor on test PCB. Pre-treatment: Heat treatment at 150+0/-10C for 1 hour, then stand at room temp for 242 hours. Test temperature: 402. Test humidity: 90%RH to 95%RH. Test time: 50024 hours. Test voltage: Rated voltage (not exceeding 630V). Voltage conditioning: 1 hour at test temp and voltage, then 242 hours at ambient conditions before measurement. |
| Life Test | Appearance: No defects or abnormalities. Capacitance Change: X5R: 12.5%. Q/DF: 7% or 2x initial value (for 16V), 5% or 2x initial value (for 25V, take larger). Insulation Resistance: 1G or R.C50s (whichever is smaller). | Mount capacitor on test substrate. Pre-treatment: Heat treatment at 150 +0/-10C for 1 hour, then stand at room temp for 24 2 hours. Test temperature: Max operating temperature 3. Test time: 100012 hours. Test voltage (life): 100% R.V. Voltage conditioning: 1 hour at test temp and voltage, then 242 hours at ambient conditions before measurement. |
Packaging Information
| Size (mm) | Carrier Tape | Reel Size | Pcs/Reel | Reels/Box | Boxes/Carton |
| 0603 | Paper Tape | 7" | 4,000 | 5 | 12 |