Specifications
Mfr. Part #:
GCNR5040-2R2NC
Package:
2020
Key Attributes
Model Number:
GCNR5040-2R2NC
Product Description
Product Overview
The GCNR5040 GLE is a magnetic component designed for various electronic applications. It features a nickel-zinc ferrite magnetic powder core and polyurethane-coated copper wire, ensuring reliable performance. This product complies with RoHS regulations.
Product Attributes
- Brand: Shenzhen Glorious Electronic Co.,Ltd.
- Origin: China (Magnetic powder, Magnetic epoxy resin, Electrode), Germany (Wire)
- Material: Nickel zinc ferrite magnetic powder, Polyurethane-system coated copper wire, Magnetic epoxy resin, Tin
- Color: Black printing
- Certifications: RoHS Comp.
Technical Specifications
| Type | Part NO. | Inductance Lo (uH) | Test Frequency (Hz/v) | DC Resistance (m)30% | Saturation Current Isat (A) Max. L/L-35% | Temperature Rise Current Irms (A) Max. T40 |
| GCNR5040 | GCNR5040-1R0M | 1.0 | 100KHz/1v | 12 | 7.35 | 4.90 |
| GCNR5040 | GCNR5040-1R5M | 1.5 | 100KHz/1v | 15 | 6.30 | 4.30 |
| GCNR5040 | GCNR5040-2R2M | 2.2 | 100KHz/1v | 19 | 4.90 | 3.80 |
| GCNR5040 | GCNR5040-3R3M | 3.3 | 100KHz/1v | 24 | 3.95 | 3.40 |
| GCNR5040 | GCNR5040-4R7M | 4.7 | 100KHz/1v | 30 | 3.50 | 3.00 |
| GCNR5040 | GCNR5040-6R8M | 6.8 | 100KHz/1v | 43 | 2.75 | 2.50 |
| GCNR5040 | GCNR5040-100M | 10 | 100KHz/1v | 64 | 2.35 | 2.10 |
| GCNR5040 | GCNR5040-150M | 15 | 100KHz/1v | 86 | 2.00 | 1.95 |
| GCNR5040 | GCNR5040-220M | 22 | 100KHz/1v | 129 | 1.60 | 1.50 |
| GCNR5040 | GCNR5040-330M | 33 | 100KHz/1v | 188 | 1.30 | 1.20 |
| GCNR5040 | GCNR5040-470M | 47 | 100KHz/1v | 272 | 1.10 | 1.00 |
| GCNR5040 | GCNR5040-680M | 68 | 100KHz/1v | 400 | 0.90 | 0.80 |
| GCNR5040 | GCNR5040-101M | 100 | 100KHz/1v | 560 | 0.75 | 0.70 |
| Item | Specification | Condition |
| Terminal Strength | No electrode detachment should be found | When the device is pushed in two directions of X and Z with the force of 5N for 102seconds after soldering between copper plate and the electrodes |
| Reflow test | Change from an initial value L : within20% | Peak temp 2405 3010s. The specimen shall be subjected to the reflow process under the above condition 2 times. Test board shall be 0.8mm thick. Base material shall be glass epoxy resin. Measurement: The specimen shall be stored at standard atmospheric conditions for 1 h in prior to the measurement. |
| Vibration | Change from an initial value L : within20% | The specimen shall be subjected to a vibration of 1.5mm amplitude, sweep frequency 10~55~10Hz after vibration for 1 hours |
| Free fall test | Change from an initial value L : within20% | The specimen must be fixed on test board. Then it shall be fallen freely from 1m height. 10 consecutive times. |
| High temperature and high humidity test | Change from an initial value L : within20% | The specimen shall be stored at a temperature of 402 with relative humidity of 90 ~ 95% for 96 4h. Then it shall be stabilized under standard atmospheric conditions for 1 h before measurement. Measurement shall be made within 1h~ 2h. |
| High temperature preservation test | Change from an initial value L : within20% | The specimen shall be stored at a temperature of 1252for 96 1h. Then it shall be stabilized under standard atmospheric conditions for 1 h before measurement. Measurement shall be made within 1h~ 2h. |
| Low temperature preservation test | Change from an initial value L : within20% | After stored at a temperature of -40 3 for 96 1h. The specimen should be measured, then it should be measured under normal temperature and humidity in 1h~ 2h hours. |
| Solder ability test | 95 . | Terminals shall be immersed in flux at room temperature. Dip sample into solder bath containing molten solder at 2605for 30.5 seconds. |
| Cold and hot cycle test | Change from an initial value L : within20% | The specimen shall be measured after 20 continuous cycles of temperature change of -403for 30 min and 1252 for 30 min with the transit period of 2min or less. Then it shall be stabilized under standard atmospheric conditions for 1 h before measurement. Measurement shall be made within 1h~ 2h. |
| Storage temperature and humidity range | temperature range 535 humidity range 25%80% | In packing state. |
2410121507_GLE-GCNR5040-2R2NC_C439372.pdf