Specifications
Current - Saturation (Isat):
2.16A
Mfr. Part #:
GCDA252010P-2R2MC
Package:
1008
Key Attributes
Model Number:
GCDA252010P-2R2MC
Product Description
Product Overview
The GCDA252010P series from Shenzhen Glorious Electronic Co.,Ltd. are magnetic components designed for various electronic applications. These components are manufactured with high-quality materials, including nickel zinc ferrite magnetic powder and polyurethane-coated copper wire, ensuring reliable performance.
Product Attributes
- Brand: GLE
- Part Number: GCDA252010P
- Origin: China (Magnetic powder, Electrode), Germany (Wire)
- Certifications: RoHS Compliant
Technical Specifications
| Part NO. | Inductance Lo (uH) | Test Frequency (Hz/v) | DC Resistance (m) max. | Saturation Current Isat (A) Max. L/L-30% | Temperature Rise Current Irms (A) Max. T-40 | Inductance Tolerance |
| GCDA252010P-R22M | 0.22 | 100KHz/1v | 12.5 | 7.2 | 5.3 | M = 20% |
| GCDA252010P-R24M | 0.24 | 100KHz/1v | 14 | 7.0 | 4.8 | M = 20% |
| GCDA252010P-R33M | 0.33 | 100KHz/1v | 26 | 6.0 | 4.0 | M = 20% |
| GCDA252010P-R47M | 0.47 | 100KHz/1v | 32 | 4.50 | 3.51 | M = 20% |
| GCDA252010P-R68M | 0.68 | 100KHz/1v | 44 | 3.87 | 3.06 | M = 20% |
| GCDA252010P-1R0M | 1.0 | 100KHz/1v | 54 | 3.15 | 2.70 | M = 20% |
| GCDA252010P-1R5M | 1.5 | 100KHz/1v | 91 | 2.34 | 2.25 | M = 20% |
| GCDA252010P-2R2M | 2.2 | 100KHz/1v | 119 | 2.16 | 2.07 | M = 20% |
| GCDA252010P-4R7M | 4.7 | 100KHz/1v | 262 | 1.62 | 1.22 | M = 20% |
General Specifications
| Item | Specification | Condition |
| Terminal Strength | No electrode detachment should be found | The device is pushed in two directions of X and Z with the force of 5N for 102seconds after soldering between copper plate and the electrodes. |
| Reflow test | L : within20% | Peak temp 2405, 3010s. The specimen shall be subjected to the reflow process under the above condition 2 times. Test board shall be 0.8mm thick. Base material shall be glass epoxy resin. |
| Vibration | L : within20% | Vibration of 1.5mm amplitude, sweep frequency 10~55~10Hz after vibration for 1 hours. |
| Free fall test | L : within20% | The specimen must be fixed on test board. Then it shall be fallen freely from 1m height, 10 consecutive times. |
| High temperature and high humidity test | L : within20% | Stored at 402, 9095% RH for 96 4h. Stabilized under standard atmospheric conditions for 1 h before measurement. Measurement within 1h~ 2h. |
| High temperature preservation test | L : within20% | Stored at 1252 for 96 1h. Stabilized under standard atmospheric conditions for 1 h before measurement. Measurement within 1h~ 2h. |
| Low temperature preservation test | L : within20% | Stored at -40 3 for 96 1h. Stabilized under standard atmospheric conditions for 1 h before measurement. Measurement within 1h~ 2h. |
| Solder ability test | 95 | Terminals immersed in flux. Dip sample into solder bath at 2605 for 30.5 seconds. |
| Cold and hot cycle test | L : within20% | 20 continuous cycles of -403 for 30 min and 1252 for 30 min with transit period of 2min or less. Stabilized under standard atmospheric conditions for 1 h before measurement. Measurement within 1h~ 2h. |
| Storage temperature and humidity range | temperature range 535, humidity range 25%80% | In packing state. |
Prohibited Substances
RoHS Regulated Substances: Lead and its compounds, Mercury and its inorganic compounds, Cadmium and its compounds, Hexavalent chromium compounds, PBB, PBDE.
Ozone Depleting Substances: CFCs, Halon, Carbon tetrachloride, Trichloroethane (Methyl chloroform).