Specifications
Voltage Rating:
25V
Capacitance:
1uF
Temperature Coefficient:
X7R
Tolerance:
±10%
Mfr. Part #:
TCC0805X7R105K250DTS
Package:
0805
Key Attributes
Model Number:
TCC0805X7R105K250DTS
Product Description
Product Overview
The S Series MLCC (Multilayer Chip Ceramic Capacitor) from CCTC is a high-performance capacitor designed with a "sandwich-structure" that offers superior mechanical strength compared to traditional designs. This enhanced durability makes it ideal for applications requiring greater resistance to bending and flexing, ensuring product reliability. The "sandwich-structure" MLCC is specifically recommended as a replacement for low capacitance conventional X7R MLCCs in demanding environments.
Product Attributes
- Brand: CCTC ()
- Origin: China
- Material: Ceramic Dielectric (X7R)
- Product Series: S Series
- Approval Sheet No.: DRAAW108E/0-2015
Technical Specifications
| Specification | Dielectrics | Technical Requirement | Testing Condition |
| Appearance | X7R | No defects or abnormalities | Visual inspection. |
| Dimensions | X7R | Within the specified dimensions | Using calipers on micrometer |
| Capacitance | X7R | Within the specified tolerance (J: 5%; K: 10%; M: 20%) | 1.00.2Vrms, 1KHz10% (Test Temp: 253, Humidity: <70%RH) |
| Dissipation Factor | X7R | DF2.5% | 1.00.2Vrms, 1KHz10% (Test Temp: 253, Humidity: <70%RH) |
| Insulation Resistance | X7R | UR 50V: More than 10 G or 500F, whichever is smaller. UR >50V: More than 4 G or 100s, whichever is smaller. | UR50V: U_test=UR, Charge Time: 605sec, Temp: 25 UR>50V: U_test=UR or 400V, Charge Time: 605sec, Temp: 25 (Test Temp: 253, Humidity: <70%RH) |
| Dielectric Strength | X7R | UR50V: Force 300%Rated voltage for 5sec. Max. current 50 mA. 100VUR<500V: Force 200%Rated voltage for 5sec. Max. current 50 mA. 500VUR<1000V: Force 150%+100V Rated voltage for 5sec. Max. current 50 mA. 1000VUR<2000V: Force 150%Rated voltage for 5sec. Max. current 50 mA. UR2000V: Force 120%Rated voltage for 5sec. Max. current 30 mA. | |
| Temperature Coefficient of Capacitance | X7R | Capacitance change within 15% | Measure capacitance under follow table list temperature: STEP 1: 25; STEP 2: -553; STEP 3: 25; STEP 4: 1253; STEP 5: 25. Capacitance change compared within the above 25 value over the temperature ranges shall be within the specified ranges. |
| Adhesion | X7R | No removal of the terminations or other defect shall occur. | The pressurizing force shall be 6N (=600g*f) and the duration of application shall be 101sec. |
| Solderability of Termination | X7R | 95% min. coverage of both terminal electrodes and less than 5% have pin holes or rough spots. | Solder temperature: 2455, Dipping time: 21 seconds. Completely soak both terminal electrodes in solder. |
| Resistance to leaching | X7R | 95% min. coverage of both terminal electrodes and less than 5% have pin holes or rough spots. No remarkable visual damage. | Solder temperature: 2705, preheated: 120~150/60sec, Dipping time: 101 seconds. Completely soak both terminal electrodes in solder. |
| Bending | X7R | No remarkable visual damage, Cp change 10% | Solder the capacitor on testing substrate and put it on testing stand. Apply pressure at 1.0mm/s rate in the direction shown in the figure, bending 1mm. |