Specifications
Voltage Rating:
50V
Capacitance:
82nF
Temperature Coefficient:
X7R
Tolerance:
±10%
Mfr. Part #:
0603X7R823K500NT
Model Number:
0603X7R823K500NT
Package:
0603
Key Attributes
Product Description
Product Overview
This specification outlines the details for high voltage MLCCs designed for applications such as coupling, wave filtering, and resonance in high voltage circuits. These components are suitable for switch power supplies, AC-DC and DC-DC power chargers, networking/communication interfaces, LCD backlight unit power supplies, and energy-saving lamps.
Product Attributes
- Material: Ceramic dielectric, Inner electrode, Outer electrode, Nickel layer, Tin layer
- Terminal Composition: Au/Ag-Ni-Sn
- Packing Options: Tape/Reel (T), Bag packing (P)
Technical Specifications
| Item | Specification/Requirement | Testing Method |
| Temperature Range | -55~+125 | |
| Visual/Dimension | 1. No Damage 2. Dimension meet Spec | Naked eye (Visual inspection) Digital calliper |
| Static Capacity | NPO characteristic: 1000pF @ 1MHz10%, 1.00.2Vrms; >1000pF @ 1KHz10%, 1.00.2Vrms X7R/X7T/X7P characteristic: 10uF @ 1KHz10%, 1.00.2Vrms; >10uF @ 120Hz24, 0.50.1Vrms | |
| Dissipation Factor (DF) | NPO Characteristic: DF0.56 (Cr5 pF); DF1.5[(150/Cr)+7]10-4 (5pFCr50pF); DF0.15% (50pFCr) X7R/X7T/X7P characteristic: See Note 1 | Cr1000pF, 110%MHz, 1V0.2rms; Cr1000pF, 110%KHz, 1V0.2rms Cr10uF, 110%KHz, 1V0.1rms; Cr10uF, 12024Hz, 0.5V0.1rms |
| IR Insulation Resistance | NPO Characteristic: IR50000M (C10nF); IR*Cr500S (C10nF) X7R/X7T/X7P Characteristic: IR10000M (C25nF); IR*Cr100S (C25nF) | Rated voltage, Time: 605s, Humidity: 75%, Temperature: 255, Current: 50mA |
| Hi-pot (DC) | No dielectric breakdown or damage | Ur=100V, 2.5x rated voltage; Ur=200V/250V, 2.0x rated voltage; Ur=450/500/630V, 1.5x rated voltage; 1KVUr2KV, 1.2x rated voltage; 2KVUr, 1.1x rated voltage. Voltage Raising time: 110S, Voltage maintaining time: 2S |
| Solderability | Soldering area90% | Pre-heating temperature 80-120, time 10-30s, lead free solder, flux. Soldering temperature 2455, Solder time 20.5s. |
| Resistance to the heat of soldering | No visual damage, soldering area90% | Pre-heating temperature 100-200, time 102 s, soldering temperature: 2655, Soldering time: 51s. Cleaning with solvent. Room temperature, time: 242 hours. |
| Electrostatic capacity change rate | NPO Characteristic: C/C0.5% or 0.5pF; X7R: C/C15%; X7T: -33% C/C22%; X7P: C/C10% | |
| Flexural strength | No damage | Base board: Al2O3 /PCB. PCB dimension: Thickness: 1.6mm, Length: 100mm, Width: 40mm. Flexural depth: 1mm, Bend speed: 0.5mm/sec. Test it under the flexural status. Electro static capacity change rate C/C10% |
| Terminal bonding strength | No visual damage | Applied Force: 5N, Duration: 101S |
| Thermal shock | NPO Characteristic: C/C2.5% or 0.25pF; X7R/X7P: C/C0.5%; X7T: C/C10% | Pre-condition(X7R h characteristic): Upper limit temperature 1hour, place 241 hours, start to testing. Run 5 cycles Thermal shock. Test it after place 242 hours normal temp & humidity. |
| Temperature moisture exposure | Visual: No visual damage. Electrostatic capacitance change rate: NPO characteristic: C/C2% or 1pF; X7R/X7T/X7P characteristic: C/C10%. DF 2 times initial standard. IR: NPO characteristic: IR2500M or IR*Cr25S; X7R/X7T/X7P: IR1000M or IR*Cr25S. | Temperature 402, Humidity 90~95%RH, time 50024 hours. Test it after place 242 hours normal temp & humidity. |
| High temperature exposure | Visual: No visual damage. Electrostatic capacitance change rate: NPO: C/C2% or 1pF; X7R/X7T/X7P: C/C20%. DF 2 X initial standard. IR: NPO: IR4000M or IR*Cr40S; X7R/X7T/X7P: IR2000M or IR*Cr50S. | Temperature 1253, Time 100048 hours. Voltage: 100VV250V (2x Rated voltage), 250VV1KV (1.5x rated voltage), 1KVV (1.2x rated voltage). Test it after place 48 hours under normal pressure & temperature. |
| PCB flexural strength | No crack and other defect | Soldering the MLCC on the PCB, Then pressing direction base on the photo. IR |