Specifications
Voltage Rating:
50V
Capacitance:
100nF
Temperature Coefficient:
M3L
Tolerance:
±5%
Mfr. Part #:
1206M3L104J500NT
Model Number:
1206M3L104J500NT
Package:
1206
Key Attributes
Product Description
Product Overview
High-voltage multilayer ceramic capacitors (MLCCs) designed for coupling, filtering, and resonant applications in high-voltage electronic circuits. Suitable for use in switching power supplies, AC-DC and DC-DC converters, network/communication interfaces, LCD module backlight power supplies, and energy-saving lamp ballasts.
Product Attributes
- Certifications: RoHS, REACH
Technical Specifications
| Item | Specification | Test Method |
| Operating Temperature Range | -55~+85 | |
| Appearance & Dimensions | No visible damage. Dimensions meet specifications. | Visual inspection for appearance. Caliper measurement for dimensions. |
| Capacitance | Within specified tolerance | Frequency: 1KHz10% (10uF), 120Hz24 (10uF) Test Voltage: 1.00.2Vrms (10uF), 0.50.1Vrms (10uF) |
| Dissipation Factor (DF) | <0.1% | Frequency: 110%KHz (Cr10uF), 12024Hz (Cr10uF) Voltage: 1V0.1rms (Cr10uF), 0.5V0.1rms (Cr10uF) |
| Insulation Resistance | >1 G | Test Voltage: 250V Test Time: 605 seconds Test Humidity: 70% Test Temperature: 255 |
| Withstand Voltage (DC) | No dielectric breakdown or damage | Test Voltage: Rated voltage Test Time: 2 seconds |
| Solderability | Tinning rate 95%, pinholes or rough areas <5%, no visible damage. | Preheat: 80-120 for 10-30 seconds. Lead-free solder, flux used. Soldering temperature: 2455, immersion time: 21 seconds. |
| Solder Heat Resistance | Appearance: No visible damage, tinning rate 95% | Preheat: 120~150/60 seconds Solder pot temperature: 2705 Immersion time: 101 seconds Both end electrodes fully immersed. Post-immersion: Solvent cleaning. Room temperature storage: 242 hours. |
| Capacitance Change Rate | -2.5% < C/C 2.5% | |
| DF Value | Same as NO4 | |
| IR | Same as NO5 | |
| Bending Strength | No visible damage. | Test substrate: Al2O3 or PCB (1.6mm thick, 100mm length, 40mm width). Bending depth: 1mm. Pressing speed: 1mm/sec. Measurement during bending. |
| Capacitance Change Rate | C/C5% | |
| Terminal Strength | No visible damage. | |
| Temperature Cycling | C/C2.5% | Pre-treatment: Upper limit temperature 1 hour, 241 hours at room temp. Initial measurement. 5 temperature cycles. 242 hours at room temp/humidity after cycles. Steps: -55 (30min), 25 (2-3min), +85 (30min), 25 (2-3min). |
| Damp Heat Resistance | No visible damage. | Test condition: 402, 90~95%RH, 50024 hours. 24 hours at room temp/humidity after test. |
| Capacitance Change Rate | C/C5% | |
| DF Value | 2 times initial standard | |
| IR | >500M | |
| High Temperature Load Test | No visible damage. | Test condition: 85, 100048 hours. Voltage: 100VV250V (1.5 times rated voltage). 242 hours at room temp/humidity after test. |
| Capacitance Change Rate | C/C5% | |
| DF Value | 2 times initial standard | |
| IR | >500M |
2507091655_AIDE-CAPACITOR-1206M3L104J500NT_C49326733.pdf