Specifications
Voltage Rating:
10V
Capacitance:
10uF
Temperature Coefficient:
X6S
Tolerance:
±20%
Mfr. Part #:
0603X6S106M100NT
Model Number:
0603X6S106M100NT
Package:
0603
Key Attributes
Product Description
Product Overview
This specification sheet details the 0603(X6S) chip ceramic capacitor, designed for high-voltage electronic circuits. It is suitable for applications such as coupling, filtering, and resonance in devices including switching power supplies, AC-DC and DC-DC converters, network/communication interfaces, LCD module backlight power supplies, and energy-saving lamp ballasts. The capacitors are manufactured using a multilayer ceramic capacitor (MLCC) structure.
Product Attributes
- Temperature Characteristics: X6S (22%)
- Termination Material: Copper/Silver-Nickel-Tin (from inside to outside)
- Environmental Compliance: RoHS Directive, REACH Regulation (SVHC)
Technical Specifications
| Item | Specification | Test Method |
|---|---|---|
| Application Range | High-voltage electronic circuits for coupling, filtering, resonance. Applications include switching power supplies, AC-DC power converters, DC-DC power converters, network/communication interfaces, LCD module backlight power supplies, energy-saving lamp ballasts. | - |
| Standard Conditions | Normal Temperature: 15~35 Normal Humidity: 45~75%RH Normal Pressure: 86~106kPa | - |
| Standard Relative Conditions | Normal Temperature: 252 Normal Humidity: 60~70%RH Normal Pressure: 86~106kPa | - |
| Product Name Composition Example | 0603 X6S 105 K 160 N T | - |
| Product Size Code | 0603 (L*W: 1.60*0.80 mm) | - |
| Nominal Capacitance | 105 (1.0 F) | - |
| Capacitance Tolerance | K (10%) | - |
| Rated Voltage (DC) | 160 (16V) | - |
| Packaging Method | T (Tape & Reel) | - |
| Product Structure | Ceramic Dielectric, Inner Electrode, Outer Electrode, Nickel Layer, Tin Layer | - |
| Product Dimensions (0603/1608) | L: 1.600.15 mm, W: 0.800.15 mm, T: 0.800.15 mm, WB: 0.300.10 mm | Vernier Caliper Measurement |
| Operating Temperature Range | -55~+105 | Visual Inspection, Vernier Caliper Measurement |
| Capacitance | Within specified tolerance | For X7R/X5R/X6S/X7S/Y5V: 10uF: 1KHz10%, 1.00.2Vrms 10uF: 120Hz24Hz, 0.50.1Vrms |
| Dissipation Factor (DF Value) | For X6S: See Note 1 | For X6S: 10uF: 1KHz10%, 1V0.1rms 10uF: 12024Hz, 0.5V0.1rms |
| Insulation Resistance (IR) | For X6S: IR10000M, C25nF; IR*C100S, C25nF | Test Voltage: 500V (if Rated Voltage 500V), Rated Voltage (if Rated Voltage <500V) Test Time: 605 sec, Humidity: 75%, Temperature: 255 |
| Withstand Voltage (DC) | 2.0 times rated voltage (for Ur=200V/250V) | Ramp time: 1~10S, Hold time: 2S |
| Solderability | Tinning rate >90%, no visible damage | Preheat: 80-120 for 10-30 sec, Lead-free solder, Flux used. Solder Temp: 2455, Solder Time: 20.5 sec. |
| Solder Heat Resistance | No visible damage, Tinning rate 90% | Preheat: 100-200 for 102 sec, Immersion Temp: 2605, Immersion Time: 51 sec. Post-cleaning and 242 hours at room temperature. |
| Capacitance Change Rate (after Solder Heat Resistance) | For X6S: |C/C| 22% | - |
| Bending Strength | No visible damage | Test Substrate: Al2O3 or PCB. Bending Depth: 1mm. Pressing Speed: 0.5mm/sec. Measurements taken under bent state. |
| Capacitance Change Rate (after Bending) | |C/C| 10% | - |
| Terminal Joint Strength | No visible damage | - |
| Temperature Cycling | For X6S: |C/C| 10% | 5 cycles. Pre-treatment for X7R: Upper temp 1 hour, 241 hours at room temp. Test after 242 hours at normal temp/humidity. |
| Damp Heat Resistance | For X6S/X5R: |C/C| 10% | Temperature: 402, Humidity: 90~95%RH, Time: 50024 hours. Test after 24 hours at normal temp/humidity. |
| DF Value (after Damp Heat) | 2 times initial standard | - |
| IR (after Damp Heat) | For X6S/X5R: IR1000M or IR*C25S (take smaller value) | - |
| High Temperature Load Test | For X6S/X5R: |C/C| 20% | Temperature: 853, Time: 100048 hours. Voltage: 1.5 times rated voltage (for 250V < V < 1KV). Test after 484 hours at normal temp/humidity. |
| DF Value (after High Temp Load) | 2 times initial standard | - |
| IR (after High Temp Load) | For X6S/X5R: IR2000M or IR*C50S (take smaller value) | - |
| PCB Bending Strength | No cracks or other defects | Welded on fixture (glass epoxy), force applied as shown in Figure 2. Reflow soldering used. |
| Packaging (Tape & Reel) | 0603: 4000 pcs 0805: 3000 pcs (T1.35mm) 1206: 3000 pcs (T1.60mm) 1210: 2000 pcs (T1.85mm) 1808: 1000 pcs (T1.85mm) 1812: 800 pcs 1812 and above: 500 pcs | - |
Note 1: DF values for X7R/X5R/X6S/X7S/Y5V characteristics are detailed in the table on page 5.
Note 2: Initial measurement for items 3, 11, 12, 13 requires preheating at 150 for 1 hour, followed by 48 hours at normal temperature and pressure.