Specifications
Voltage Rating:
16V
Capacitance:
10uF
Temperature Coefficient:
X6S
Tolerance:
±10%
Mfr. Part #:
0805X6S106K160NT
Model Number:
0805X6S106K160NT
Package:
0805
Key Attributes
Product Description
Product Overview
This specification sheet details 0805(X6S) chip ceramic capacitors designed for high-voltage electronic circuits. They are suitable for coupling, filtering, and resonant applications, commonly found in switching power supplies, AC-DC and DC-DC converters, network/communication interfaces, LCD module backlight power supplies, and energy-saving lamp ballasts. These high-voltage MLCCs offer reliable performance across various demanding electronic systems.
Product Attributes
- Temperature Characteristics: X6S (22%)
- Termination Material: Copper/Silver-Nickel-Tin (from inside to outside)
- Environmental Compliance: RoHS Directive, REACH Regulation (SVHC)
Technical Specifications
| Item | Specification | Test Method |
|---|---|---|
| Application Range | High-voltage electronic circuits for coupling, filtering, resonance. Applications include switching power supplies, AC-DC converters, DC-DC converters, network/communication interfaces, LCD module backlight power supplies, energy-saving lamp ballasts. | - |
| Standard Conditions | Ambient Temperature: 15~35 Ambient Humidity: 45~75%RH Ambient Pressure: 86~106kPa | - |
| Standard Relative Conditions | Ambient Temperature: 252 Ambient Humidity: 60~70%RH Ambient Pressure: 86~106kPa | - |
| Product Structure & Dimensions | Structure: Ceramic Dielectric, Internal Electrode, External Electrode, Nickel Layer, Tin Layer. Dimensions (0805/2012): L: 2.000.20mm, W: 1.250.20mm, T: 0.800.20mm, WB: 1.000.20mm | Visual inspection for appearance; Vernier caliper for dimensions. |
| Operating Temperature Range | -55~+105 | - |
| Appearance & Dimensions | 1. No visible damage. 2. Dimensions meet specifications. | Visual inspection; Vernier caliper measurement. |
| Capacitance | Within specified tolerance. | NPO: 1000pF @ 1MHz10%, 1.00.2Vrms; >1000pF @ 1KHz10%, 1.00.2Vrms. X7R/X7T/X5R: 10uF @ 1KHz10%, 1.00.2Vrms; >10uF @ 120Hz24, 0.50.1Vrms. |
| Dissipation Factor (DF Value) | NPO: DF0.56% (Cr5pF); DF1.5[(150/Cr)+7]10-4 (5pFCr50pF); DF0.15% (50pFCr). Measured at 110%MHz, 1V0.2rms for Cr1000pF; 110%KHz, 1V0.2rms for Cr1000pF. X7R/X5R/X6S/X7S/Y5V: See Note 1. Measured at 110%KHz, 1V0.1rms for Cr10uF; 12024Hz, 0.5V0.1rms for Cr10uF. | - |
| Insulation Resistance (IR) | NPO: IR50000M (C10nF); IR*Cr500S (C10nF). Test Voltage: 500V (Rated voltage 500V) or Rated voltage (Rated voltage 500V). Test time: 605 sec. Humidity: 75%. Temperature: 255. Charge/discharge current: 50mA. X7R/X6S/X5R: IR10000M (C25nF); IR*Cr100S (C25nF). | - |
| Dielectric Strength (DC) | No dielectric breakdown or damage. Test voltage is a multiple of rated voltage (Ur): 2.5x (Ur=100V), 2.0x (Ur=200V/250V), 1.5x (Ur=450/500/630V), 1.2x (1KVUr2KV), 1.1x (Ur2KV). Ramp time: 1-10S. Hold time: 2S. | - |
| Solderability | Soldering rate >90%. No visible damage. Preheating: 80-120 for 10-30 sec. Lead-free solder, flux used. Solder temperature: 2455. Soldering time: 20.5 sec. | - |
| Solder Heat Resistance | Appearance: No visible damage, soldering rate 90%. Preheating: 100-200 for 102 sec. Immersion temperature: 2605. Immersion time: 51 sec. Clean with solvent. Store at room temperature for 242 hours. Capacitance Change Rate: NPO: |C/C|0.5% or 0.5pF (whichever is greater). X7R: |C/C|15%. X7T: -33% C/C22%. X6S: |C/C|22%. DF Value: As per No. 4. IR: As per No. 5. | - |
| Bending Strength | No visible damage. Test substrate: Al2O3 or PCB (1.6mm thickness, 100mm length, 40mm width). Bending depth: 1mm. Pressing speed: 0.5mm/sec. Capacitance Change Rate: |C/C|10%. | - |
| Terminal Connection Strength | No visible damage. | - |
| Temperature Cycling | NPO: |C/C|2.5% or 0.25pF (whichever is greater). X7R/X5R: |C/C|7.5%. X6S: |C/C|10%. Pre-treatment (X7R): 1 hour at upper temp, 241 hours at ambient. 5 cycles. Post-test: 242 hours at ambient conditions. Steps: Lower temp (303 min), Ambient (2-3 min), Upper temp (303 min), Ambient (2-3 min). | - |
| Damp Heat Resistance | Appearance: No visible damage. Post-test: 24 hours at ambient conditions. Temperature: 402 Humidity: 90~95%RH Time: 50024 hours. Capacitance Change Rate: NPO: |C/C|2% or 1pF (whichever is greater). X7R/X6S/X5R: |C/C|10%. DF Value: 2x initial standard. IR: NPO: IR2500M or IR*Cr25S (whichever is smaller). X7R/X6S/X5R: IR1000M or IR*Cr25S (whichever is smaller). | - |
| High Temperature Load Test | Appearance: No visible damage. Charge/discharge current: 50mA. Post-test: 484 hours at ambient conditions. Temperature: 853 Time: 100048 hours. Voltage: 2x rated voltage (100VV250V), 1.5x rated voltage (250VV1KV), 1.2x rated voltage (1KVV). Capacitance Change Rate: NPO: |C/C|2% or 1pF (whichever is greater). X7R/X6S/X5R: |C/C|20%. DF Value: 2x initial standard. IR: NPO: IR4000M or IR*Cr40S (whichever is smaller). X7R/X6S/X5R: IR2000M or IR*Cr50S (whichever is smaller). | - |
| Circuit Board Bending Performance | No cracks or other defects. Soldering via reflow. | - |
| Packaging (Tape & Reel) | 0805 (2012): 3000 pcs (T1.35mm), 3000 pcs (T1.35mm) 1206 (3216): 2000 pcs (T1.60mm), 3000 pcs (T1.60mm) 1210 (3225): 2000 pcs (T1.85mm), 1000 pcs (T1.85mm) 1808 (4520): 800 pcs 1812 (4532): 500 pcs | - |
| Packaging (Paper Tape) | 1005 (0402): 4000 pcs 0603: 4000 pcs 0805: 4000 pcs | - |