Specifications
Voltage Rating:
6.3V
Capacitance:
22uF
Temperature Coefficient:
X6S
Tolerance:
±20%
Mfr. Part #:
0603X6S226M6R3NT
Model Number:
0603X6S226M6R3NT
Package:
0603
Key Attributes
Product Description
Product Overview
This specification sheet details the 0603 (X6S) surface mount ceramic capacitor (MLCC) designed for high-voltage electronic circuits. It is suitable for applications such as coupling, filtering, and resonance in switching power supplies, AC-DC and DC-DC converters, network/communication interfaces, LCD module backlight power supplies, and energy-saving lamp ballasts. The capacitors are manufactured with a multi-layer ceramic structure, featuring internal electrodes, external electrodes, a nickel layer, and a tin layer.
Product Attributes
- Temperature Characteristics: X6S (22%)
- Termination Material: Copper/Silver-Nickel-Tin (from inside to outside)
- Compliance: RoHS Directive, REACH Regulation (SVHC)
Technical Specifications
| Item | Specification | Test Method |
|---|---|---|
| Application Range | High-voltage electronic circuits for coupling, filtering, resonance. Applications include switching power supplies, AC-DC converters, DC-DC converters, network/communication interfaces, LCD module backlight power supplies, and energy-saving lamp ballasts. | - |
| Standard Conditions | Ambient Temperature: 15~35 Ambient Humidity: 45~75%RH Ambient Pressure: 86~106kPa | - |
| Standard Relative Conditions | Ambient Temperature: 252 Ambient Humidity: 60~70%RH Ambient Pressure: 86~106kPa | - |
| Product Name Composition | Example: 0603 X6S 105 K 160 N T Product Size Code Temperature Characteristic Nominal Capacitance Capacitance Tolerance Rated Voltage (DC) Termination Material Packaging Method | - |
| Product Structure | Ceramic Dielectric Internal Electrode External Electrode Nickel Layer Tin Layer | - |
| Product Dimensions (0603) | Model: 0603 (1608) Dimensions (mm): L: 1.600.15, W: 0.800.15, T: 0.800.15, WB: 0.300.10 | Vernier Caliper Measurement |
| Operating Temperature Range | -55~+105 | - |
| Appearance and Dimensions | 1. No visible damage. 2. Dimensions meet specifications. | Visual inspection; Vernier caliper measurement. |
| Capacitance | Within specified tolerance. (See Note 1 for initial value measurement) | Frequency and voltage as per NPO or X7R/X5R/X6S/X7S/Y5V characteristics. |
| Dissipation Factor (DF Value) | X6S characteristics: See Note 1. | Frequency and voltage as per X7R/X5R/X6S/X7S/Y5V characteristics. |
| Insulation Resistance (IR) | X6S characteristics: IR 10000M, C 25nF; IR*C 100S, C > 25nF. | Test voltage: 500V DC or rated voltage (whichever is lower). Test time: 605 sec. Humidity: 75%. Temperature: 255. |
| Dielectric Withstanding Voltage (DC) | No dielectric breakdown or damage. Test voltage is 1.5 to 2.5 times rated voltage depending on Ur. | Voltage applied for 2 sec. Ramp time: 1-10 sec. |
| Solderability | Tinning rate > 90%. No visible damage. | Preheat 80-120 for 10-30 sec. Lead-free solder, flux. Solder temp: 2455. Soldering time: 20.5 sec. |
| Solder Heat Resistance | No visible damage, tinning rate 90%. Capacitance change rate for X6S: |C/C| 22%. DF value and IR as per initial standard. | Preheat 100-200 for 102 sec. Immersion temp: 2605. Immersion time: 51 sec. Conditioned at room temp for 242 hours. |
| Bending Strength | No visible damage. Capacitance change rate: |C/C| 10%. | Test substrate (Al2O3 or PCB) bent to 1mm depth at 0.5mm/sec. Measurement in bent state. |
| Terminal Pull Strength | No visible damage. | - |
| Temperature Cycling | Capacitance change rate for X6S: |C/C| 10%. | 5 cycles of temperature extremes (-55 to +105). Conditioned at room temp/humidity for 242 hours before testing. |
| Damp Heat Resistance | No visible damage. Capacitance change rate for X6S: |C/C| 10%. DF value 2x initial standard. IR for X6S: IR 1000M or IR*C 25S (whichever is smaller). | 402, 90-95%RH for 50024 hours. Conditioned at room temp/humidity for 24 hours after test. |
| High Temperature Load Test | No visible damage. Capacitance change rate for X6S: |C/C| 20%. DF value 2x initial standard. IR for X6S: IR 2000M or IR*C 50S (whichever is smaller). | 853 for 100048 hours. Voltage applied is 1.5 to 2 times rated voltage depending on Ur. Charge/discharge current limited to 50mA. Conditioned at room temp/humidity for 484 hours after test. |
| Circuit Board Bending Test | No cracks or defects. | Capacitor soldered onto fixture, then subjected to bending force. |
| Packaging (Tape & Reel) | 0603: 4000 pcs 0805: 3000 pcs (T1.35mm) 1206: 3000 pcs (T1.60mm) 1210: 2000 pcs (T1.85mm) 1808: 1000 pcs (T1.85mm) 1812: 800 pcs (T1.85mm) | - |
Note 1: Initial value measurement for capacitance, DF, and IR requires preheating at 150 for 1 hour, followed by 48 hours at room temperature and standard pressure.
Note 2: DF values for X7R/X5R/X6S/X7S/Y5V characteristics are detailed in a separate table (Page 6).