Specifications
Voltage Rating:
25V
Capacitance:
2.2uF
Temperature Coefficient:
X6S
Tolerance:
±10%
Mfr. Part #:
0603X6S225K250NT
Model Number:
0603X6S225K250NT
Package:
0603
Key Attributes
Product Description
Product Overview
This specification sheet details the 0603(X6S) surface mount ceramic capacitors (MLCCs) designed for high-voltage electronic circuits. They are suitable for applications such as coupling, filtering, and resonance in switching power supplies, AC-DC and DC-DC converters, network/communication interfaces, LCD module backlight power supplies, and energy-saving lamp ballasts.
Product Attributes
- Temperature Characteristics: X6S (22%)
- Termination Material: Copper/Silver-Nickel-Tin (from inside to outside)
- Environmental Compliance: RoHS Directive, REACH Regulation (SVHC)
Technical Specifications
| Item | Specification | Test Method |
|---|---|---|
| Application Range | High-voltage electronic circuits for coupling, filtering, resonance. Applications include switching power supplies, AC-DC power converters, DC-DC power converters, network/communication interfaces, LCD module backlight power supplies, energy-saving lamp ballasts. | - |
| Standard Conditions | Ambient Temperature: 15~35 Ambient Humidity: 45~75%RH Ambient Pressure: 86~106kPa | - |
| Standard Relative Conditions | Ambient Temperature: 252 Ambient Humidity: 60~70%RH Ambient Pressure: 86~106kPa | - |
| Product Code Structure | Example: 0603 X6S 105 K 160 N T Product Size Code Temperature Characteristic Nominal Capacitance Capacitance Tolerance Rated Voltage (DC) Termination Material Packaging Method | - |
| Product Size Codes & Dimensions | 0603: L*W (inch) 0.06*0.03, L*W (mm) 1.60*0.80 0805: L*W (inch) 0.08*0.05, L*W (mm) 2.00*1.25 1206: L*W (inch) 0.12*0.06, L*W (mm) 3.20*1.60 1210: L*W (inch) 0.12*0.10, L*W (mm) 3.20*2.50 1808: L*W (inch) 0.18*0.08, L*W (mm) 4.50*2.00 1812: L*W (inch) 0.18*0.12, L*W (mm) 4.50*3.20 | - |
| Product Structure | Ceramic Dielectric Inner Electrode Outer Electrode Nickel Layer Tin Layer | - |
| Product Dimensions (0603/1608) | L: 1.600.15 mm, W: 0.800.15 mm, T: 0.800.15 mm, WB: 0.300.10 mm | - |
| Operating Temperature Range | -55~+105 | Visual inspection for appearance. Vernier caliper for dimensions. |
| Capacitance | Within specified tolerance. NPO: 1000pF @ 1MHz10%, 1.00.2Vrms; >1000pF @ 1KHz10%, 1.00.2Vrms X7R/X7T/X5R: 10uF @ 1KHz10%, 1.00.2Vrms; >10uF @ 120Hz24, 0.50.1Vrms | - |
| Dissipation Factor (DF Value) | NPO: DF0.56%, Cr5 pF; DF1.5[(150/Cr)+7]10-4 (5pFCr50pF); DF0.15%, (50pFCr) X7R/X5R/X6S/X7S/Y5V: See Note 1. Cr10uF @ 1KHz10%, 1V0.1rms; Cr10uF @ 12024Hz, 0.5V0.1rms | - |
| Insulation Resistance | NPO: IR50000M, C10nF; IR*Cr500S, C10nF X7R/X6S/X5R: IR10000M, C25nF; IR*Cr100S, C25nF | Test Voltage: 500V (if Rated Voltage 500V), or Rated Voltage (if Rated Voltage <500V). Test Time: 605 sec. Test Humidity: 75%. Test Temperature: 255. Test Charge/Discharge Current: 50mA. |
| Dielectric Strength (DC) | No dielectric breakdown or damage. 100V Ur: 2.5 x Rated Voltage 200V/250V Ur: 2.0 x Rated Voltage 450/500/630V Ur: 1.5 x Rated Voltage 1KV Ur 2KV: 1.2 x Rated Voltage 2KV < Ur: 1.1 x Rated Voltage | Voltage rising time: 1-10S. Holding time: 2S. |
| Solderability | Tinning rate >90%. No visible damage. | Preheat at 80-120 for 10-30 sec. Lead-free solder, flux used. Solder temperature: 2455. Soldering time: 20.5 sec. |
| Solder Heat Resistance | Appearance: No visible damage, tinning rate 90%. Capacitance Change Rate: NPO: |C/C| 0.5% or 0.5pF (whichever is greater) X7R: |C/C| 15% X7T: -33% C/C 22% X6S: |C/C| 22% DF Value: Same as NO4 IR: Same as NO5 | Preheat at 100-200 for 102 sec. Immersion temperature: 2605. Immersion time: 51 sec. Clean with solvent. Store at room temperature for 242 hours before testing. |
| Bending Strength | Appearance: No visible damage. Capacitance Change Rate: |C/C| 10% | Test substrate: Al2O3 or PCB. PCB dimensions: Thickness: 1.6mm, Length: 100mm, Width: 40mm. Bending depth: 1mm. Pressing speed: 0.5mm/sec. Measurements to be taken under bent condition. |
| Terminal Bond Strength | No visible damage. | - |
| Temperature Cycling | NPO: |C/C| 2.5% or 0.25pF (whichever is greater) X7R/X5R: |C/C| 7.5% X6S: |C/C| 10% | Pre-conditioning (X7R): Upper temperature for 1 hour, store for 241 hours, initial measurement. 5 temperature cycles performed. Store at room temp/humidity for 242 hours after cycles, then test. Steps: Lower temp (303 min), Room temp/humidity (2-3 min), Upper temp (303 min), Room temp/humidity (2-3 min). |
| Damp Heat Resistance | Appearance: No visible damage. Capacitance Change Rate: NPO: |C/C| 2% or 1pF (whichever is greater) X7R/X6S/X5R: |C/C| 10% DF Value: 2x initial standard IR: NPO: IR2500M or IR*Cr25S (whichever is smaller) X7R/X6S/X5R: IR1000M or IR*Cr25S (whichever is smaller) | Test Conditions: Temperature 402, Humidity 90~95%RH, Time 50024 hours. Store at room temp/humidity for 24 hours after test, then measure. |
| High Temperature Load Test | Appearance: No visible damage. Capacitance Change Rate: NPO: |C/C| 2% or 1pF (whichever is greater) X7R/X6S/X5R: |C/C| 20% DF Value: 2x initial standard IR: NPO: IR4000M or IR*Cr40S (whichever is smaller) X7R/X6S/X5R: IR2000M or IR*Cr50S (whichever is smaller) | Pre-conditioning: Store at room temp/humidity for 484 hours before test. Test Conditions: Temperature 853, Time 100048 hours. Voltage: 100V V 250V: 2 x Rated Voltage 250V < V < 1KV: 1.5 x Rated Voltage 1KV V: 1.2 x Rated Voltage Charge/discharge current limited to below 50mA. |
| PCB Bending Performance | No cracks or other defects. | Capacitors soldered onto fixture (glass epoxy) using hybrid solder. Force applied as per diagram 2 after soldering. Soldering by reflow, avoiding uneven soldering and thermal shock. |
| Packaging (Pieces per reel) | Paper Tape Packaging: 0603: 4000 0805: 4000 1005: 4000 0201: 4000 Tape Packaging: 0805 (T1.35mm): 3000 1206 (T1.60mm): 3000 1210 (T1.85mm): 2000 1808: 1000 1812 (T1.85mm): 1000 2220: 800 2225: 500 | - |
Note 1: X7R/X5R/X6S/X7S/Y5V DF Exception details are provided in the original document and vary based on rated voltage and capacitance values.
Note 2: Initial measurement for items NO3, 11, 12, 13 requires preheating at 150 for 1 hour, followed by storage at room temperature and pressure for 48 hours.
2507091655_AIDE-CAPACITOR-0603X6S225K250NT_C49326392.pdf
Request A Quote
Please Use Our Online Inquiry Contact Form Below If You Have Any Questions, Our Team Will Get Back To You As Soon As Possible